SAE J403 Grade 12L14
Equivalent material: DIN 1.0737, DIN 9SMnPb36, DIN 11SMnPb37, AFNOR S300Pb, AFNOR 11SMnPb37, BS 11SMnPb37, SS 1926, AISI 12L14, JIS SUM24L, JIS 12SMnPb35, EN 11SMnPb37, EN 1.0737, ISO 11SMnPb37, ISO 12SMnPb35, ASTM 12L14, UNS G12144, DIN 1.0718, DIN 9SMnPb28, DIN 11SMnPb30, AFNOR S250Pb, AFNOR 11SMnPb30, BS 11SMnPb30, UNI CF9SMnPb28, SS 1914, UNE 11SMnPb28, AISI 1215, AISI 12L13, SAE 1215, SAE 12L13, JIS SUM22L, JIS SUM23L, JIS 11SMnPb28, EN 11SMnPb30, EN 1.0718, ISO 11SMnPb30, ISO 11SMnPb28, GB/T U72152, GB/T Y15Pb, UNS G12134, UNS G12150
SAE J403 Grade 12L14 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
SAE J403 Grade 12L14 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
SAE J403 Grade 12L14 chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.02 % |
| Carbon |
Carbon of 0.15 % |
| Chromium |
Chromium of 0.02 % |
| Copper |
Copper of 0.02 % |
| Iron |
balance |
| Lead |
Lead of 0.15 - 0.35 % |
| Manganese |
Manganese of 0.85 - 1.15 % |
| Molybdenum |
Molybdenum of 0.02 % |
| Nickel |
Nickel of 0.02 % |
| Niobium |
Niobium of 0.08 % |
| Phosphorus |
Phosphorus of 0.04 - 0.09 % |
| Silicon |
Silicon of 0.02 % |
| Sulfur |
Sulfur of 0.26 - 0.35 % |
| Titanium |
Titanium of 0.08 % |
| Vanadium |
Vanadium of 0.08 % |
SAE J403 Grade 12L14 magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
SAE J403 Grade 12L14 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
SAE J403 Grade 12L14 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |