DIN 1651 Grade 9SMnPb36 untreated
DIN 1651 Grade 9SMnPb36 untreated introduction
The balanced high performance machining steel 9 SMnPb 36 shows an excellent cutting behaviour. Because of the S content a lower toughness and a increased crack danger.
Application: mass components in the automotive engineering, toolbuilding, apparatus engineering
Equivalent material: AFNOR S300Pb, ISO 12SMnPb35, UNI CF9SMnPb36, JIS SUM24L, SS 1914-04, VSM 9SMnPb36, UNE F.2114-12SMnPb35, SAE 12L14, DIN 11SMnPb37, DIN 1.0737, AFNOR 11SMnPb37, BS 11SMnPb37, SS 1926, AISI 12L14, JIS 12SMnPb35, EN 11SMnPb37, EN 1.0737, ISO 11SMnPb37, ASTM 12L14, UNS G12144
DIN 1651 Grade 9SMnPb36 untreated general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
DIN 1651 Grade 9SMnPb36 untreated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.1E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.18E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 460 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 480 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 520 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 610 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 54.4 W/(m·K) |
- |
DIN 1651 Grade 9SMnPb36 untreated chemical
| Property |
Value |
| Carbon |
Carbon of 0.15 % |
| Lead |
Lead of 0.15 - 0.35 % |
| Manganese |
Manganese of 1.1 - 1.5 % |
| Phosphorus |
Phosphorus of 0.1 % |
| Silicon |
Silicon of 0.05 % |
| Sulfur |
Sulfur of 0.34 - 0.4 % |
DIN 1651 Grade 9SMnPb36 untreated magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
DIN 1651 Grade 9SMnPb36 untreated electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.1E-7 Ω·m |
DIN 1651 Grade 9SMnPb36 untreated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 210 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 193 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 185 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 175 GPa |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 156 - 174 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 360 - 590 MPa |
- |