DIN 1651 Grade 10SPb20 untreated
DIN 1651 Grade 10SPb20 untreated introduction
The fully killed machining steel 10 SPb 20 shows a better machinability because of the Pb and S additions.
Application in the case hardened condition for thin-walled parts in the automotive engineering, toolbuilding, apparatus engineering.
Equivalent material: GB Y12Pb, ISO 10SPb20, UNI CF10SPb20, JIS SUM12, SS 1914-04, UNE F.2112-10SPb20, SAE 11L08, DIN 1.0722, AFNOR 10SPb20, BS 10SPb20, AISI 11L08, JIS 10SPb20, EN 10SPb20, EN 1.0722, GB/T U72122, GB/T Y12Pb
DIN 1651 Grade 10SPb20 untreated general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
DIN 1651 Grade 10SPb20 untreated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.1E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.18E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 460 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 480 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 520 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 600 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 52.4 W/(m·K) |
- |
DIN 1651 Grade 10SPb20 untreated chemical
| Property |
Value |
| Carbon |
Carbon of 0.07 - 0.13 % |
| Lead |
Lead of 0.15 - 0.35 % |
| Manganese |
Manganese of 0.7 - 1.1 % |
| Phosphorus |
Phosphorus of 0.06 % |
| Silicon |
Silicon of 0.1 - 0.3 % |
| Sulfur |
Sulfur of 0.18 - 0.25 % |
DIN 1651 Grade 10SPb20 untreated magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
DIN 1651 Grade 10SPb20 untreated electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.1E-7 Ω·m |
DIN 1651 Grade 10SPb20 untreated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 210 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 193 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 185 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 175 GPa |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 146 - 159 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 350 - 530 MPa |
- |
Tailor-made steel solutions to meet your unique requirements.