EN 10277-3 Grade 11SMnPb37 as rolled and turned (+SH)
EN 10277-3 Grade 11SMnPb37 as rolled and turned (+SH) introduction
Free cutting steel 11SMnPb37 is a very-high-performance free cutting steel of excellent machining properties. It is unsuitable for heat-treatment. Deteriorating ductility qualities due to increased S-content and higher cracking risk have to be considered. 11SMnPb37 shows compared to 11SMn37 better parameter. Application for bulk parts in car industry, in apparatus and equipment engineering. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).
Equivalent material: AFNOR S300Pb, ISO 12SMnPb35, UNI CF9SMnPb36, JIS SUM24L, SS 1914-04, VSM 9SMnPb36, UNE F.2114-12SMnPb35, SAE 12L14, DIN 9SMnPb36, AS 12L14, ISO 11SMnPb37, ASTM 12L14, UNS G12144, DIN 1.0737, DIN 11SMnPb37, AFNOR 11SMnPb37, BS 11SMnPb37, SS 1926, AISI 12L14, JIS 12SMnPb35, EN 1.0737
EN 10277-3 Grade 11SMnPb37 as rolled and turned (+SH) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
EN 10277-3 Grade 11SMnPb37 as rolled and turned (+SH) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.1E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.18E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 460 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 480 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 520 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 610 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 54.4 W/(m·K) |
- |
EN 10277-3 Grade 11SMnPb37 as rolled and turned (+SH) chemical
| Property |
Value |
| Carbon |
Carbon of 0.14 % |
| Lead |
Lead of 0.2 - 0.35 % |
| Manganese |
Manganese of 1 - 1.5 % |
| Phosphorus |
Phosphorus of 0.11 % |
| Silicon |
Silicon of 0.05 % |
| Sulfur |
Sulfur of 0.34 - 0.4 % |
EN 10277-3 Grade 11SMnPb37 as rolled and turned (+SH) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10277-3 Grade 11SMnPb37 as rolled and turned (+SH) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.1E-7 Ω·m |
EN 10277-3 Grade 11SMnPb37 as rolled and turned (+SH) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 210 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 193 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 185 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 175 GPa |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 107 - 169 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 360 - 570 MPa |
- |
Let your imagination run wild as you discover the endless design possibilities our steel offers.
-- Our promise