JIS G4804 Grade 12SMnPb35 cold-drawn
Equivalent material: DIN 1.0737, DIN 9SMnPb36, DIN 11SMnPb37, AFNOR S300Pb, AFNOR 11SMnPb37, BS 11SMnPb37, SS 1926, AISI 12L14, SAE 12L14, JIS SUM24L, EN 11SMnPb37, EN 1.0737, ISO 11SMnPb37, ISO 12SMnPb35, ASTM 12L14, UNS G12144
JIS G4804 Grade 12SMnPb35 cold-drawn general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
JIS G4804 Grade 12SMnPb35 cold-drawn thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
JIS G4804 Grade 12SMnPb35 cold-drawn magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
JIS G4804 Grade 12SMnPb35 cold-drawn electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
JIS G4804 Grade 12SMnPb35 cold-drawn mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 7 - 10 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 390 - 840 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 255 - 430 MPa |
- |