JIS G3313 Grade CR2
Equivalent material: DIN 1.0347, DIN RRSt 3, DIN RRSt 13, DIN St 13, DIN St 13 O3, DIN St 13 03, DIN DC03, AFNOR E, AFNOR XE, AFNOR DC03, BS DC03, BS CS1, BS CS3, AISI 1008, SAE 1008, JIS SPCD, JIS SECE, EN DC03, EN FeP03, EN 1.0347, ISO CR2, GOST 08Ju, GB/T LT 03, GB/T U43074, ASTM A 619
JIS G3313 Grade CR2 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
JIS G3313 Grade CR2 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
JIS G3313 Grade CR2 magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
JIS G3313 Grade CR2 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
JIS G3313 Grade CR2 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 31 % |
- |
| Elongation A80 |
23.0 °C |
Elongation A80 of 30 % |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 57 [-] |
- |
| Hardness, Rockwell Superficial 30-T |
23.0 °C |
Hardness, Rockwell Superficial 30-T of 55 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 370 MPa |
- |