AISI 1008 Hot Rolled
Equivalent material: DIN 1.0204, DIN C11G1C, DIN UQSt 36, DIN StE 420, DIN TStE 420, DIN S420N, SAE 1008, JIS SPHT1, JIS SV34, JIS SV330, JIS SWRY11, EN S420N, EN 1.0204, GOST 08kp, ASTM 1008, ASTM M1008, UNS G10080, IS 4C2, DIN 1.0211, DIN St 30 Si, DIN S215GSiT, BS HFW 2, JIS STAM290GA, JIS STAM290GB, EN 1.0211, DIN 1.0304, DIN C9D, AFNOR C9D, BS C9D, JIS SWRM8K, JIS SWRM8, JIS HR2, EN C9D, EN 1.0304, DIN 1.0318, DIN St 28, JIS 12B, JIS STKM12B, EN 1.0318, DIN 1.0330, DIN St 12, DIN St 2, DIN DC01, AFNOR DC01, BS DC01, JIS SPCC, JIS SECD, EN DC01, EN 1.0330, ISO CR1, ISO HR1, ISO 02, GOST 08kp-3, GB/T LT 02, GB/T U43084, ASTM A366, DIN 1.0332, DIN StW 22, DIN DC11, AFNOR DC11, AFNOR 1C, BS DC11, BS 4CS, BS 4HS, BS 4CR, JIS SPHC, JIS SPHD, JIS SEHD, EN DD11, EN 1.0332, ISO HR2, GOST 15kp, ASTM CS Type B, DIN 1.0347, DIN RRSt 3, DIN RRSt 13, DIN St 13, DIN St 13 O3, DIN St 13 03, DIN DC03, AFNOR E, AFNOR XE, AFNOR DC03, BS DC03, BS CS1, BS CS3, JIS SPCD, JIS SECE, JIS CR2, EN DC03, EN FeP03, EN 1.0347, ISO CR2, GOST 08Ju, GB/T LT 03, GB/T U43074, ASTM A 619, DIN 1.0398, DIN RRStW 23, DIN DD12, AFNOR 2C, AFNOR DD12, BS HR3:DD12, JIS HR3, EN DD12, EN 1.0398, ISO HR3, DIN 1.1113, DIN C8D2, AFNOR C8D2, BS C8D2, EN C8D2, EN 1.1113, ISO C8D2, GB/T C8D2, ASTM Grade 1008
AISI 1008 Hot Rolled general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.9 g/cm³ |
AISI 1008 Hot Rolled thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
AISI 1008 Hot Rolled chemical
| Property |
Value |
| Carbon |
Carbon of 0 - 0.1 % |
| Iron |
Iron of 99.31 - 99.7 % |
| Manganese |
Manganese of 0.3 - 0.5 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Sulfur |
Sulfur of 0 - 0.05 % |
AISI 1008 Hot Rolled magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
AISI 1008 Hot Rolled electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
AISI 1008 Hot Rolled mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 210 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 32 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 330 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 180 MPa |
- |