JIS G3141 Grade SPCC 1/4 hard
Equivalent material: GB H08A, GB H08E, GOST Ст1кп, GOST 08kp, GOST 08Yu, GOST 08пс, GOST 08ps, GOST St1kp, GOST БСт1кп, GOST ВСт1кп, AS HRC, AS K1008, AS R1008, AS S1008, AS C1008, AS ICRC, AS Hd1, AS CX1, EN DC01, DIN St2, DIN UQSt36, DIN St12, NF XC6FF, NF XC6, BS 4HR, BS 4HS, BS 4CR, BS 4CS, BS 261, IS 2879, IS C05, IS C07, UNI 3CD8, UNI CB10FU, ÖNORM UC10, ÖNORM RC10, ÖNORM St02F, ÖNORM St02FK32, ÖNORM St02FK40, ÖNORM St02FK50, ÖNORM St02FK60, ÖNORM St02FK70, UNE AP00, UNE AP02, SIS 1142-42, SIS 1146-32, SIS 1146-42, SIS 1147-32, SIS 1147-42, SIS 1225-00, SIS 1225-01, SIS 1232-03, SIS 1232-04, SIS 1232-08, SIS 1311-00, SIS 1311-10, SIS 1142, SIS 1146, SIS 1232-05, SIS 1232-06, ASTM 1008, ASTM M1008, MIL 1008, MIL CS1008, JIS SV330, AISI 1008, AISI M1008, SAE 1008, DIN St30Si, DIN St30Al, DIN St28, DIN 1.0330, DIN St 12, DIN St 2, DIN DC01, AFNOR DC01, BS DC01, JIS SECD, EN 1.0330, ISO CR1, ISO HR1, ISO 02, GOST 08kp-3, GB/T LT 02, GB/T U43084, ASTM A366, UNS G10080
JIS G3141 Grade SPCC 1/4 hard general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
JIS G3141 Grade SPCC 1/4 hard thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
JIS G3141 Grade SPCC 1/4 hard magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
JIS G3141 Grade SPCC 1/4 hard electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
JIS G3141 Grade SPCC 1/4 hard mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 32 - 39 % |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 65 - 80 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 115 - 150 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 270 MPa |
- |