DIN 17111 Grade UQSt 36 hot rolled

DIN 17111 Grade UQSt 36 hot rolled

DIN 17111 Grade UQSt 36 hot rolled introduction

The steel is suitable for cold heading and is used for the manufacture of bolts, nuts and rivets (and similar shaped parts).

Equivalent material: AS 1008, IS 1148, JIS SV34, JIS SV330, AISI 1008, SAE 1008, UNS G10080, ASTM 1008, DIN 1.0204, DIN C11G1C, DIN StE 420, DIN TStE 420, DIN S420N, JIS SPHT1, JIS SWRY11, EN S420N, EN 1.0204, GOST 08kp, ASTM M1008, IS 4C2

DIN 17111 Grade UQSt 36 hot rolled general

Property Temperature Value
Density 20.0 °C Density of 7.85 g/cm³

DIN 17111 Grade UQSt 36 hot rolled thermal

Property Temperature Value Comment
Coefficient of thermal expansion -100.0 °C Coefficient of thermal expansion of 1.08E-5 1/K -
- 20.0 °C Coefficient of thermal expansion of 1.19E-5 1/K -
- 100.0 °C Coefficient of thermal expansion of 1.25E-5 1/K -
- 200.0 °C Coefficient of thermal expansion of 1.3E-5 1/K -
- 300.0 °C Coefficient of thermal expansion of 1.36E-5 1/K -
- 400.0 °C Coefficient of thermal expansion of 1.41E-5 1/K -
- 500.0 °C Coefficient of thermal expansion of 1.45E-5 1/K -
- 600.0 °C Coefficient of thermal expansion of 1.49E-5 1/K -
Max service temperature - Max service temperature of 500 °C Typical for Carbon Steel
Melting point - Melting point of 1480 - 1526 °C Typical for Low Carbon Steel
Specific heat capacity -100.0 °C Specific heat capacity of 423 J/(kg·K) -
- 20.0 °C Specific heat capacity of 461 J/(kg·K) -
- 100.0 °C Specific heat capacity of 479 J/(kg·K) -
- 200.0 °C Specific heat capacity of 499 J/(kg·K) -
- 300.0 °C Specific heat capacity of 517 J/(kg·K) -
- 400.0 °C Specific heat capacity of 536 J/(kg·K) -
- 500.0 °C Specific heat capacity of 558 J/(kg·K) -
- 600.0 °C Specific heat capacity of 587 J/(kg·K) -
Thermal conductivity 20.0 °C Thermal conductivity of 56.9 W/(m·K) -
- 100.0 °C Thermal conductivity of 56.4 W/(m·K) -
- 200.0 °C Thermal conductivity of 53.5 W/(m·K) -
- 300.0 °C Thermal conductivity of 49.4 W/(m·K) -
- 400.0 °C Thermal conductivity of 45.2 W/(m·K) -
- 500.0 °C Thermal conductivity of 41.3 W/(m·K) -
- 600.0 °C Thermal conductivity of 37.6 W/(m·K) -
Thermal diffusivity 20.0 °C Thermal diffusivity of 15.7 mm²/s -
- 100.0 °C Thermal diffusivity of 14.5 mm²/s -
- 200.0 °C Thermal diffusivity of 12.9 mm²/s -
- 300.0 °C Thermal diffusivity of 11.2 mm²/s -
- 400.0 °C Thermal diffusivity of 9.6 mm²/s -
- 500.0 °C Thermal diffusivity of 7.9 mm²/s -
- 600.0 °C Thermal diffusivity of 6.3 mm²/s -

DIN 17111 Grade UQSt 36 hot rolled chemical

Property Value
Carbon Carbon of 0.14 %
Manganese Manganese of 0.25 - 0.5 %
Phosphorus Phosphorus of 0.04 %
Sulfur Sulfur of 0.04 %

DIN 17111 Grade UQSt 36 hot rolled magnetic

Property Value Comment
Curie temperature Curie temperature of 770 °C Typical for Low Carbon Steel

DIN 17111 Grade UQSt 36 hot rolled electrical

Property Temperature Value
Electrical resistivity 20.0 °C Electrical resistivity of 1.83E-7 Ω·m
- 100.0 °C Electrical resistivity of 2.27E-7 Ω·m
- 200.0 °C Electrical resistivity of 2.95E-7 Ω·m
- 300.0 °C Electrical resistivity of 3.8E-7 Ω·m
- 400.0 °C Electrical resistivity of 4.81E-7 Ω·m
- 500.0 °C Electrical resistivity of 5.99E-7 Ω·m
- 600.0 °C Electrical resistivity of 7.38E-7 Ω·m

DIN 17111 Grade UQSt 36 hot rolled mechanical

Property Temperature Value Comment
Elastic modulus -100.0 °C Elastic modulus of 217 GPa -
- 20.0 °C Elastic modulus of 212 GPa -
- 100.0 °C Elastic modulus of 207 GPa -
- 200.0 °C Elastic modulus of 199 GPa -
- 300.0 °C Elastic modulus of 192 GPa -
- 400.0 °C Elastic modulus of 184 GPa -
- 500.0 °C Elastic modulus of 175 GPa -
- 600.0 °C Elastic modulus of 164 GPa -
Elongation 20.0 °C Elongation of 30 % -
Poisson's ratio 23.0 °C Poisson's ratio of 0.29 [-] Typical for Low Carbon Steel
Shear modulus 23.0 °C Shear modulus of 82 GPa Typical for Low Carbon Steel
Tensile strength 20.0 °C Tensile strength of 330 - 430 MPa -
Yield strength 20.0 °C Yield strength of 195 - 205 MPa -