ASTM A513 Grade 1008 Sink-Drawn
Equivalent material: DIN 1.0211, DIN St 30 Si, DIN S215GSiT, BS HFW 2, AISI 1008, SAE 1008, JIS STAM290GA, JIS STAM290GB, EN 1.0211, DIN 1.0318, DIN St 28, JIS 12B, JIS STKM12B, EN 1.0318, UNS G10080, DIN 1.0204, DIN C11G1C, DIN UQSt 36, DIN StE 420, DIN TStE 420, DIN S420N, JIS SPHT1, JIS SV34, JIS SV330, JIS SWRY11, EN S420N, EN 1.0204, GOST 08kp, ASTM M1008, IS 4C2, DIN 1.1113, DIN C8D2, AFNOR C8D2, BS C8D2, EN C8D2, EN 1.1113, ISO C8D2, GB/T C8D2, ASTM Grade 1008
ASTM A513 Grade 1008 Sink-Drawn general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ASTM A513 Grade 1008 Sink-Drawn thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
ASTM A513 Grade 1008 Sink-Drawn chemical
| Property |
Value |
| Carbon |
Carbon of 0.1 % |
| Manganese |
Manganese of 0.5 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Sulfur |
Sulfur of 0.035 % |
ASTM A513 Grade 1008 Sink-Drawn magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ASTM A513 Grade 1008 Sink-Drawn electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A513 Grade 1008 Sink-Drawn mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 8 % |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 65 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 330 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 260 MPa |
- |