EN 10152 Grade DC01 skin passed
EN 10152 Grade DC01 skin passed introduction
EN DC01 is ideal for deep drawing and resistant to static stress. It's known for its excellent forming performance, processing consistency and high rigidity. Its good formability enables cold forming operations
Equivalent material: IS CR1, IS SECD, ASTM A1008CSTypeA, ASTM CSTypeA, DIN St2, DIN St12, DIN St12O3, DIN St12-03, AFNOR C, BS CR4, IS SECC, SS 14-11-42, ASTM CSTypeA.BorC, DIN St12ZE, AS CA1, IS D, IS SPCC, DIN 1.0330, EN DC01+Z, EN FeP01, EN 1.0330, DIN St 12, DIN St 2, DIN St 12-03, DIN DC01, AFNOR DC01, UNI FeP01, AISI 1006, BS DC01, SAE 1006, JIS SPCC, JIS SECD, ISO CR1, ISO HR1, ISO 02, GOST 08kp-3, GB/T LT 02, GB/T U43084, ASTM A366, ASTM 1006, UNS G10080
EN 10152 Grade DC01 skin passed general
| Property |
Value |
Comment |
| Density |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10152 Grade DC01 skin passed thermal
| Property |
Value |
Comment |
| Coefficient of thermal expansion |
Coefficient of thermal expansion of 1.32e-05 - 1.38e-05 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
Max service temperature of 322.1 °C |
Predicted Value, Long |
| - |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
EN 10152 Grade DC01 skin passed chemical
| Property |
Value |
Condition |
Related Standards |
Shape |
| Carbon |
Carbon of 0.12 % |
skin passed |
EN 10152 |
Strip, Sheet |
| Manganese |
Manganese of 0.6 % |
skin passed |
EN 10152 |
Strip, Sheet |
| Phosphorus |
Phosphorus of 0.045 % |
skin passed |
EN 10152 |
Strip, Sheet |
| Sulfur |
Sulfur of 0.045 % |
skin passed |
EN 10152 |
Strip, Sheet |
EN 10152 Grade DC01 skin passed magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10152 Grade DC01 skin passed electrical
| Property |
Value |
Comment |
| Electrical conductivity |
Electrical conductivity of 8 S/m |
Predicted Value |
| Electrical resistivity |
Electrical resistivity of 1.43e-07 - 1.74e-07 Ω·m |
Typical for Carbon Steel |
EN 10152 Grade DC01 skin passed mechanical
| Property |
Temperature |
Value |
Condition |
Related Standards |
Shape |
Comment |
| Elastic modulus |
- |
Elastic modulus of 200 - 215 GPa |
- |
- |
- |
Typical for Low Carbon Steel |
| Elongation |
- |
Elongation of 14.4 % |
- |
- |
- |
Predicted Value, A200 |
| - |
- |
Elongation of 19.8 % |
- |
- |
- |
Predicted Value, A50 |
| - |
- |
Elongation of 20.0 % |
- |
- |
- |
Predicted Value, A5 |
| - |
- |
Elongation of 20.4 % |
- |
- |
- |
Predicted Value, Transverse |
| - |
- |
Elongation of 20.9 % |
- |
- |
- |
Predicted Value |
| - |
20 °C |
Elongation of 24 % |
skin passed |
EN 10152 |
Strip |
A80 Transverse |
| - |
20 °C |
Elongation of 26 % |
skin passed |
EN 10152 |
Strip |
A80 Transverse |
| - |
20 °C |
Elongation of 28 % |
skin passed |
EN 10152 |
Strip |
A80 Transverse |
| - |
20 °C |
Elongation of 28 % |
skin passed |
EN 10152 |
Strip, Sheet |
A80 |
| Hardness, Brinell |
- |
Hardness, Brinell of 261 [-] |
- |
- |
- |
Predicted Value, Transverse |
| Poisson's ratio |
- |
Poisson's ratio of 0.29 [-] |
- |
- |
- |
Typical for Low Carbon Steel |
| Reduction of area |
- |
Reduction of area of 41.3 % |
- |
- |
- |
Predicted Value |
| - |
- |
Reduction of area of 43.8 % |
- |
- |
- |
Predicted Value, Transverse |
| Shear modulus |
- |
Shear modulus of 82 GPa |
- |
- |
- |
Typical for Low Carbon Steel |
| Shear strength |
- |
Shear strength of 527 MPa |
- |
- |
- |
Predicted Value |
| Tensile strength |
20 °C |
Tensile strength of 270 - 410 MPa |
skin passed |
EN 10152 |
Strip |
Transverse |
| - |
20 °C |
Tensile strength of 270 - 410 MPa |
skin passed |
EN 10152 |
Strip, Sheet |
- |
| Yield strength |
- |
Yield strength of 278 MPa |
- |
- |
- |
Predicted Value, RP05 |
| - |
- |
Yield strength of 285.1 MPa |
- |
- |
- |
Predicted Value, RP1 Transverse |
| - |
- |
Yield strength of 293.7 MPa |
- |
- |
- |
Predicted Value, RP1 |
| - |
- |
Yield strength of 376.6 MPa |
- |
- |
- |
Predicted Value, RP02 Transverse |
| - |
- |
Yield strength of 538.2 MPa |
- |
- |
- |
Predicted Value, RP02 |
| - |
- |
Yield strength of 626.3 MPa |
- |
- |
- |
Predicted Value, RP002 |
| - |
20 °C |
Yield strength of 140 - 320 MPa |
skin passed |
EN 10152 |
Strip |
Transverse |
| - |
20 °C |
Yield strength of 140 - 300 MPa |
skin passed |
EN 10152 |
Strip |
Transverse |
| - |
20 °C |
Yield strength of 140 - 280 MPa |
skin passed |
EN 10152 |
Strip |
Transverse |
| - |
20 °C |
Yield strength of 140 - 280 MPa |
skin passed |
EN 10152 |
Strip, Sheet |
- |