DIN 5512-2 Grade DC01 skin passed
DIN 5512-2 Grade DC01 skin passed introduction
The steel is used for rail vehicle and container engineering acc. to the selected standard DIN 5512-2.
The corresponding properties of EN 10130 shall be taken.
Equivalent material: AS CA1, BS CR4, BS CS4, IS D, JIS SPCC, ASTM CSTypeA, DIN 1.0330, DIN St 12, DIN St 2, AFNOR DC01, BS DC01, AISI 1008, SAE 1008, JIS SECD, EN DC01, EN 1.0330, ISO CR1, ISO HR1, ISO 02, GOST 08kp-3, GB/T LT 02, GB/T U43084, ASTM A366, UNS G10080
DIN 5512-2 Grade DC01 skin passed general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
DIN 5512-2 Grade DC01 skin passed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
DIN 5512-2 Grade DC01 skin passed chemical
| Property |
Value |
| Carbon |
Carbon of 0.12 % |
| Manganese |
Manganese of 0.6 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Sulfur |
Sulfur of 0.045 % |
DIN 5512-2 Grade DC01 skin passed magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
DIN 5512-2 Grade DC01 skin passed electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
DIN 5512-2 Grade DC01 skin passed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A80 |
20.0 °C |
Elongation A80 of 28 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 270 - 410 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 140 - 280 MPa |
- |
Partner with us to achieve engineering excellence by leveraging our high-performance steel materials.