EN 10139 Grade DC01 work hardened (C390)
EN 10139 Grade DC01 work hardened (C390) introduction
DC01 Steel grade cold rolled according to EN 10139 - C390 with improved hardness. Suitable for Automotive componentes, Domestic Appliances, Tubes, Radiators and others. Mechanical properties should be garanteed for up to three months after manufacturing. Condition C390 should be suitable for welding, but the microstructure and mechanical properties could be affected during welding.
Equivalent material: SAE 1008, SAE 1010, DIN FeP01, DIN St12, JIS SPCC, AFNOR C, AFNOR F12, AFNOR FeP01, BS CR4, BS FeP01, EN FeP01, UNI FeP01, UNE AP00, GB 08, GB 08F, SS 1142, CSN 11321, ONORM St02F, GOST 08kp, GOST 08ps, ISO Cr01, ISO CR22, IS O, IS 2879, IS C05, IS C07, DIN 1.0330, DIN 1.0330, DIN St 12, DIN St 2, DIN DC01, AFNOR DC01, BS DC01, AISI 1008, JIS SPCC, JIS SECD, EN 1.0330, ISO CR1, ISO HR1, ISO 02, GOST 08kp-3, GB/T LT 02, GB/T U43084, ASTM A366, UNS G10080
EN 10139 Grade DC01 work hardened (C390) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10139 Grade DC01 work hardened (C390) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 22 W/(m·K) |
- |
EN 10139 Grade DC01 work hardened (C390) chemical
| Property |
Value |
| Carbon |
Carbon of 0.12 % |
| Manganese |
Manganese of 0.6 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Sulfur |
Sulfur of 0.045 % |
EN 10139 Grade DC01 work hardened (C390) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10139 Grade DC01 work hardened (C390) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
EN 10139 Grade DC01 work hardened (C390) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 117 - 172 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 390 - 540 MPa |
- |