EN 10139 Grade DC03 soft annealed (+A)
EN 10139 Grade DC03 soft annealed (+A) introduction
Cold rolled uncoated low carbon steel narrow strip for cold forming.
Equivalent material: AS CA2, GB DC03, IS CR3, ISO CR2, JIS SPCD, GOST 08Ju, GOST 08Ю, ASTM A1008DSTypeA, ASTM A1008DSTypeB, ASTM DSTypeA, ASTM DSTypeB, DIN RRSt3, DIN RRSt13, DIN St13, DIN St13O3, DIN St13-03, DIN 1.0336, DIN USt 4, DIN USt 14, AFNOR E, BS CR2, BS CR3, UNI FeP02, UNE AP02, EN FeP03, EN 1.0336, GOST 08kp, GOST 08ps, DIN 1.0347, DIN RRSt 3, DIN RRSt 13, DIN St 13, DIN St 13 O3, DIN St 13 03, DIN DC03, AFNOR XE, AFNOR DC03, BS DC03, BS CS1, BS CS3, AISI 1008, SAE 1008, JIS SECE, JIS CR2, EN 1.0347, GB/T LT 03, GB/T U43074, ASTM A 619
EN 10139 Grade DC03 soft annealed (+A) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10139 Grade DC03 soft annealed (+A) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
EN 10139 Grade DC03 soft annealed (+A) chemical
| Property |
Value |
| Carbon |
Carbon of 0.1 % |
| Manganese |
Manganese of 0.45 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Sulfur |
Sulfur of 0.035 % |
EN 10139 Grade DC03 soft annealed (+A) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10139 Grade DC03 soft annealed (+A) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
EN 10139 Grade DC03 soft annealed (+A) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A50 |
20.0 °C |
Elongation A50 of 36 % |
- |
| Elongation A80 |
20.0 °C |
Elongation A80 of 34 % |
- |
| Hardness, Vickers |
20.0 °C |
Hardness, Vickers of 100 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 270 - 370 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 140 MPa |
- |