JIS G3141 Grade SPCD 1/4 hard
Equivalent material: DIN 1.0336, DIN USt 4, DIN USt 14, AFNOR E, BS CR2, BS CR3, UNI FeP02, UNE AP02, EN DC03, EN FeP03, EN 1.0336, GOST 08kp, GOST 08ps, DIN 1.0347, DIN RRSt 3, DIN RRSt 13, DIN St 13, DIN St 13 O3, DIN St 13 03, DIN DC03, AFNOR XE, AFNOR DC03, BS DC03, BS CS1, BS CS3, AISI 1008, SAE 1008, JIS SECE, JIS CR2, EN 1.0347, ISO CR2, GOST 08Ju, GB/T LT 03, GB/T U43074, ASTM A 619
JIS G3141 Grade SPCD 1/4 hard general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
JIS G3141 Grade SPCD 1/4 hard thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
JIS G3141 Grade SPCD 1/4 hard magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
JIS G3141 Grade SPCD 1/4 hard electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
JIS G3141 Grade SPCD 1/4 hard mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 34 - 41 % |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 65 - 80 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 115 - 150 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 270 MPa |
- |