ISO 16120-2 Grade C9D
ISO 16120-2 Grade C9D introduction
Non-alloy steel wire rod for drawing and/or cold rolling for general purpose wire rod (e.g. application for springs, steel wire).
Equivalent material: GB C9D, GB U53092, IS 3, ISO C9D, JIS SWRM8, ASTM A510 Grade 1008, UNS G10080, DIN 1.0304, DIN C9D, AFNOR C9D, BS C9D, AISI 1008, SAE 1008, JIS SWRM8K, JIS HR2, EN 1.0304
ISO 16120-2 Grade C9D general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ISO 16120-2 Grade C9D thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
ISO 16120-2 Grade C9D chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.01 % |
| Carbon |
Carbon of 0.1 % |
| Chromium |
Chromium of 0.2 % |
| Copper |
Copper of 0.3 - 0.35 % |
| Manganese |
Manganese of 0.3 - 0.6 % |
| Molybdenum |
Molybdenum of 0.05 - 0.08 % |
| Nickel |
Nickel of 0.25 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.3 % |
| Sulfur |
Sulfur of 0.035 % |
ISO 16120-2 Grade C9D magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ISO 16120-2 Grade C9D electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ISO 16120-2 Grade C9D mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
Our state-of-the-art manufacturing ensures precision and impeccable finishes.
-- Our promise