EN 10139 Grade DC01 cold-rolled, strain-hardened (C290)
EN 10139 Grade DC01 cold-rolled, strain-hardened (C290) introduction
Cold rolled uncoated low carbon steel narrow strip for cold forming.,The non-alloy steel DC01 acc. to DIN EN 10130 is suitable for cold forming of simple profile forms and components. Mechanical foldings are possible for thicknesses of up to 1,5 mm. To freedom of stretcher strains applies a period of 3 months after provision of the products for surface type B.
Welding:
DC01 is weldable by the following welding methods: MAG (metal-active-gas), plasma welding, laser welding, compression weld welding, resistance welding (spot, roll weld, buckle welding), arc welding.
The steel acts as substrate for surface refined and coated bands and sheets.
Application of DC01: household appliances industry, construction trade, car manufacturing, traffic system.
Acc. to DIN EN 10139 DC01 is offered as cold rolled band or bar, cut in strength range HK270 to HK690. On welding of DC01in condition HK290 to HK690 has to be considered the potential influence to the mechanical properties
Equivalent material: AS CA1, GB DC01, IS CR2, ISO CR1, ISO CR22, JIS SPCC, ASTM A1008CSTypeA, ASTM CSTypeA, DIN St2, DIN St12, DIN St12O3, DIN St12-03, IS D, DIN 1.0330, DIN St 12, DIN St 2, DIN DC01, AFNOR DC01, BS DC01, AISI 1008, SAE 1008, JIS SECD, EN 1.0330, ISO HR1, ISO 02, GOST 08kp-3, GB/T LT 02, GB/T U43084, ASTM A366, UNS G10080
EN 10139 Grade DC01 cold-rolled, strain-hardened (C290) general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10139 Grade DC01 cold-rolled, strain-hardened (C290) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
EN 10139 Grade DC01 cold-rolled, strain-hardened (C290) chemical
| Property |
Value |
| Carbon |
Carbon of 0.12 % |
| Manganese |
Manganese of 0.6 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Sulfur |
Sulfur of 0.045 % |
EN 10139 Grade DC01 cold-rolled, strain-hardened (C290) electrical
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10139 Grade DC01 cold-rolled, strain-hardened (C290) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation |
20.0 °C |
Elongation of 24 % |
- |
| Elongation A50 |
20.0 °C |
Elongation A50 of 20 % |
- |
| Elongation A80 |
20.0 °C |
Elongation A80 of 18 % |
- |
| Hardness, Vickers |
20.0 °C |
Hardness, Vickers of 95 - 125 [-] |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 290 - 430 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 200 - 380 MPa |
- |