EN 10277-5 Grade Cm60 cold drawn or turned and soft annealed
EN 10277-5 Grade Cm60 cold drawn or turned and soft annealed introduction
Steel Cm 60 is suitable for high strained parts in vehicle manufacturing, engine and machine engineering that require an enhanced workability while maintaining strength qualities (e.g. gear wheels, pinion, shafts). Lowest application temp. -25 °C.
Equivalent material: NBN C60-3, BS 070M60, ISO C60M2, DIN C60R, DIN 1.1223, DIN Cm 60, AFNOR C60R, BS C60R, AISI 1060, SAE 1060, EN C60R, EN 1.1223, ISO C60R, UNS G10600
EN 10277-5 Grade Cm60 cold drawn or turned and soft annealed general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
EN 10277-5 Grade Cm60 cold drawn or turned and soft annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.11E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.21E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.29E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.35E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Max service temperature, long |
- |
Max service temperature, long of -25 - 0 °C |
- |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 486 J/(kg·K) |
Typical for High Carbon Steel |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 51 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 49.9 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 47.8 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 44.8 W/(m·K) |
- |
EN 10277-5 Grade Cm60 cold drawn or turned and soft annealed chemical
| Property |
Value |
| Carbon |
Carbon of 0.57 - 0.65 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.02 - 0.035 % |
EN 10277-5 Grade Cm60 cold drawn or turned and soft annealed electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.3E-7 Ω·m |
EN 10277-5 Grade Cm60 cold drawn or turned and soft annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 210 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 205 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 195 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 185 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 175 GPa |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 241 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
- |