EN 10277-5 Grade Cm60 cold drawn or turned and normalized

EN 10277-5 Grade Cm60 cold drawn or turned and normalized introduction

Steel Cm 60 is suitable for high strained parts in vehicle manufacturing, engine and machine engineering that require an enhanced workability while maintaining strength qualities (e.g. gear wheels, pinion, shafts). Lowest application temp. -25 °C.

Equivalent material: NBN C60-3, BS 070M60, ISO C60M2, DIN C60R, DIN 1.1223, DIN Cm 60, AFNOR C60R, BS C60R, AISI 1060, SAE 1060, EN C60R, EN 1.1223, ISO C60R, UNS G10600

EN 10277-5 Grade Cm60 cold drawn or turned and normalized general

Property Temperature Value
Density 20.0 °C Density of 7.85 g/cm³

EN 10277-5 Grade Cm60 cold drawn or turned and normalized thermal

Property Temperature Value Comment
Coefficient of thermal expansion 100.0 °C Coefficient of thermal expansion of 1.11E-5 1/K -
- 200.0 °C Coefficient of thermal expansion of 1.21E-5 1/K -
- 300.0 °C Coefficient of thermal expansion of 1.29E-5 1/K -
- 400.0 °C Coefficient of thermal expansion of 1.35E-5 1/K -
Max service temperature - Max service temperature of 500 °C Typical for Carbon Steel
Max service temperature, long - Max service temperature, long of -25 - 0 °C -
Melting point - Melting point of 1289 - 1478 °C Typical for High Carbon Steel
Specific heat capacity 23.0 °C Specific heat capacity of 486 J/(kg·K) Typical for High Carbon Steel
Thermal conductivity 20.0 °C Thermal conductivity of 51 W/(m·K) -
- 100.0 °C Thermal conductivity of 49.9 W/(m·K) -
- 200.0 °C Thermal conductivity of 47.8 W/(m·K) -
- 300.0 °C Thermal conductivity of 44.8 W/(m·K) -

EN 10277-5 Grade Cm60 cold drawn or turned and normalized chemical

Property Value
Carbon Carbon of 0.57 - 0.65 %
Manganese Manganese of 0.6 - 0.9 %
Phosphorus Phosphorus of 0.04 %
Silicon Silicon of 0.4 %
Sulfur Sulfur of 0.02 - 0.035 %

EN 10277-5 Grade Cm60 cold drawn or turned and normalized electrical

Property Temperature Value
Electrical resistivity 20.0 °C Electrical resistivity of 1.3E-7 Ω·m

EN 10277-5 Grade Cm60 cold drawn or turned and normalized mechanical

Property Temperature Value Comment
Elastic modulus 20.0 °C Elastic modulus of 210 GPa -
- 100.0 °C Elastic modulus of 205 GPa -
- 200.0 °C Elastic modulus of 195 GPa -
- 300.0 °C Elastic modulus of 185 GPa -
- 400.0 °C Elastic modulus of 175 GPa -
Elongation 20.0 °C Elongation of 10 - 11 % -
Poisson's ratio 23.0 °C Poisson's ratio of 0.29 [-] Typical for High Carbon Steel
Shear modulus 20.0 °C Shear modulus of 81 GPa -
Tensile strength 20.0 °C Tensile strength of 670 - 710 MPa -
Yield strength 20.0 °C Yield strength of 340 - 380 MPa -