EN 10132-3 Grade C60E cold rolled (+CR)
EN 10132-3 Grade C60E cold rolled (+CR) introduction
Cold-rolled narrow strip made of the mild steel C60E will be delivered in thicknesses up to 6 mm for quenching and tempering and for quenched and tempered cold strip in thicknesses between 0.3 mm and 3.0 mm in following conditions:
- soft annealed or soft annealed and little rerolled (+A or +LC),
- cold rolled (+CR),
- quenched and tempered (+QT).
The delivery condition annealed to globular carbides (+AC) can be agreed.
Equivalent material: GB 60, GB U20602, ISO CS60, JIS S60CM, ASTM A684 Grade 1055, UNS G10550, DIN Ck60, DIN 1.1221, DIN C60E, AFNOR XC60, AFNOR C60RR, AFNOR 9160C031, AFNOR 9160/C25, AFNOR XC65, AFNOR C60E, BS 060A62, BS 070M60, BS CS60, BS C60E, BS 60HS, BS 60CS, UNI C60, SS 1678, AISI 1060, 1064, SAE 1060, JIS S58C, JIS S65CM, JIS S60C-CSP, JIS S65C-CSP, JIS S65C, JIS 30A, JIS 37A, EN C60S, EN 1.1221, ISO C60E, ISO C60E4, ISO S58C, GOST 60, GOST 60G, GOST 60GA, GB/T 60, GB/T CRB970, GB/T U20602, ASTM 1060, UNS G10600, UNS G10640
EN 10132-3 Grade C60E cold rolled (+CR) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.8 - 7.85 g/cm³ |
EN 10132-3 Grade C60E cold rolled (+CR) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.11E-5 - 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.21E-5 - 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.29E-5 - 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.35E-5 - 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 41.7 - 51 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 43.4 - 49.9 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 43.2 - 47.8 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 41.4 - 44.8 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 39.1 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 36.7 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 34.1 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 11.6 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 11.3 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 10.5 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 9.5 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.3 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.1 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 5.8 mm²/s |
- |
EN 10132-3 Grade C60E cold rolled (+CR) chemical
| Property |
Value |
| Carbon |
Carbon of 0.57 - 0.65 % |
| Chromium |
Chromium of 0.4 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 0.4 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
EN 10132-3 Grade C60E cold rolled (+CR) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.3E-7 - 2.5E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.95E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.65E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.53E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.56E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.74E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 8.13E-7 Ω·m |
EN 10132-3 Grade C60E cold rolled (+CR) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 210 - 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 205 - 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 195 - 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 185 - 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 175 - 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Hardness, Vickers |
20.0 °C |
Hardness, Vickers of 255 - 305 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 1050 - 1100 MPa |
- |
Experience the power of our steel, meticulously crafted to withstand the toughest challenges and meet the highest industry standards.