EN 10277-5 Grade C60R cold drawn and quenched and tempered (+C+QT)
EN 10277-5 Grade C60R cold drawn and quenched and tempered (+C+QT) introduction
Steel C60R is suitable for high loaded parts in vehicle, engine and machine engineering with enhanced workability at constant strength qualities (e.g. gear wheels, pinions, shafts). Lowest application temperature -25°C.
As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).
Equivalent material: NBN C60-3, BS 070M60, ISO C60M2, DIN Cm60, ISO C60R, ASTM A108 Grade 1060, SAE 1060, SAE Grade 1060, UNS G10600, DIN 1.1223, DIN Cm 60, DIN C60R, AFNOR C60R, BS C60R, AISI 1060, EN 1.1223
EN 10277-5 Grade C60R cold drawn and quenched and tempered (+C+QT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
EN 10277-5 Grade C60R cold drawn and quenched and tempered (+C+QT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.11E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.21E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.29E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.35E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Max service temperature, long |
- |
Max service temperature, long of -25 - 0 °C |
- |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 486 J/(kg·K) |
Typical for High Carbon Steel |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 51 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 49.9 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 47.8 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 44.8 W/(m·K) |
- |
EN 10277-5 Grade C60R cold drawn and quenched and tempered (+C+QT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.57 - 0.65 % |
| Chromium |
Chromium of 0.4 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 0.4 % |
| Phosphorus |
Phosphorus of 0.03 - 0.04 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.02 - 0.04 % |
EN 10277-5 Grade C60R cold drawn and quenched and tempered (+C+QT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.3E-7 Ω·m |
EN 10277-5 Grade C60R cold drawn and quenched and tempered (+C+QT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 210 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 205 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 195 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 185 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 175 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 13 - 14 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 750 - 950 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 450 - 520 MPa |
- |