EN 10216-3 Grade P460N normalized or normalized formed (+N)
EN 10216-3 Grade P460N normalized or normalized formed (+N) introduction
Steel P460N is a weldable fine-grained construction steel (alloyed high-grade steel) for pressure vessel construction.
Equivalent material: DIN StE460, DIN 1.8905, DIN StE 460, DIN P460N, BS P460N, JIS SM53B, JIS SM53C, JIS SM520B, JIS SM520C, JIS E460DD, EN 1.8905, ISO E460DD, ASTM F70, ASTM A612, ASTM Grade LF6 Class 1
EN 10216-3 Grade P460N normalized or normalized formed (+N) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.84 g/cm³ |
EN 10216-3 Grade P460N normalized or normalized formed (+N) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.05E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.15E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.21E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.27E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.4E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.44E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
-100.0 °C |
Thermal conductivity of 34.7 W/(m·K) |
- |
| - |
20.0 °C |
Thermal conductivity of 39.7 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 40.9 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 41 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 39.9 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 38.2 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 36.1 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 33.8 W/(m·K) |
- |
| Thermal diffusivity |
-100.0 °C |
Thermal diffusivity of 11.9 mm²/s |
- |
| - |
20.0 °C |
Thermal diffusivity of 11 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 10.5 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 9.9 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 9.1 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.1 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 6.9 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 5.7 mm²/s |
- |
EN 10216-3 Grade P460N normalized or normalized formed (+N) chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.02 % |
| Carbon |
Carbon of 0.2 % |
| Chromium |
Chromium of 0.3 % |
| Copper |
Copper of 0.7 % |
| Manganese |
Manganese of 1 - 1.7 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 0.8 % |
| Niobium |
Niobium of 0.05 % |
| Nitrogen |
Nitrogen of 0.02 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.6 % |
| Sulfur |
Sulfur of 0.02 % |
| Titanium |
Titanium of 0.04 % |
| Vanadium |
Vanadium of 0.2 % |
EN 10216-3 Grade P460N normalized or normalized formed (+N) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10216-3 Grade P460N normalized or normalized formed (+N) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
-100.0 °C |
Electrical resistivity of 1.97E-7 Ω·m |
| - |
20.0 °C |
Electrical resistivity of 2.62E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 3.13E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.85E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.7E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.69E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.85E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 8.2E-7 Ω·m |
EN 10216-3 Grade P460N normalized or normalized formed (+N) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 200 - 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 19 % |
- |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 17 % |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.29 [-] |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 490 - 730 MPa |
- |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 490 - 730 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 390 - 460 MPa |
- |
| Yield strength, transverse |
20.0 °C |
Yield strength, transverse of 390 - 460 MPa |
- |
Optimize your operations with our efficient steel solutions, designed to enhance productivity and reduce costs.
-- Our promise