EN 10277-2 Grade St52-3 cold drawn
EN 10277-2 Grade St52-3 cold drawn introduction
St 52-3 is a higher strength fine grained steel and used for high dynamic loaded welded constructions up to a temperature of -20 °C.
Equivalent material: NBN AE355D, AFNOR E36-4, BS 50D, GOST S345, ISO Fe510-D, UNI Fe510D, JIS SM53C, ÖNORM St510D, SS 2134-01, UNE A510D, ASTM 50, DIN 1.0570, DIN St 52-3, DIN S355J2, DIN Fe 510 D1, DIN St 52-3 G, DIN S355J2G3, DIN S325G, AFNOR TU E 355 4, AFNOR TS E 355 4, AFNOR S355J2G3, AFNOR E36-3, BS 50 D, BS S355J2G3, AISI 345A, AISI 1024, SAE 345A, SAE 1024, JIS SKK490, JIS SM50, JIS SM53, JIS SM490, JIS SM520, JIS STK50, JIS STK51, JIS STK490, JIS STK500, JIS STKR50, JIS STKR490, JIS SM490A, JIS SM490B, JIS SM490C, JIS SM490YA, JIS SM490YB, JIS SM520B, JIS SM520C, JIS SKY490, EN S355J2, EN 1.0570, ISO S355D, GOST 17G1S, GOST 17GS, GB/T 16MnDR, GB/T L20173, GB/T 16Mn, GB/T L20166, UNS K02003, UNS K03011, UNS K03014, UNS K12037, UNS K12709, IS Fe540W-HT
EN 10277-2 Grade St52-3 cold drawn general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.83 g/cm³ |
EN 10277-2 Grade St52-3 cold drawn thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Max service temperature, long |
- |
Max service temperature, long of -20 - 300 °C |
- |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
-100.0 °C |
Thermal conductivity of 37.6 W/(m·K) |
- |
| - |
20.0 °C |
Thermal conductivity of 42.2 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 43.2 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 42.9 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 41.2 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 39.1 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 36.6 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 34.1 W/(m·K) |
- |
| Thermal diffusivity |
-100.0 °C |
Thermal diffusivity of 12.9 mm²/s |
- |
| - |
20.0 °C |
Thermal diffusivity of 11.7 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 11.2 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 10.3 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 9.4 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.3 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.1 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 5.7 mm²/s |
- |
EN 10277-2 Grade St52-3 cold drawn chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.02 % |
| Carbon |
Carbon of 0.2 % |
| Manganese |
Manganese of 1.6 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.55 % |
| Sulfur |
Sulfur of 0.04 % |
EN 10277-2 Grade St52-3 cold drawn magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10277-2 Grade St52-3 cold drawn electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
-100.0 °C |
Electrical resistivity of 1.82E-7 Ω·m |
| - |
20.0 °C |
Electrical resistivity of 2.47E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.96E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.68E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.55E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.56E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.75E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 8.13E-7 Ω·m |
EN 10277-2 Grade St52-3 cold drawn mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 5 - 10 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 500 - 1000 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 325 - 600 MPa |
- |