EN 10213 Grade G17Mn5 quenched and tempered (+QT)
EN 10213 Grade G17Mn5 quenched and tempered (+QT) introduction
Material G17Mn5 is roughly the same as make GS-16 Mn 5 acc. to DIN 17182-92. It is applicated at low temperatures for pressure vessels.
Equivalent material: DIN GS-16Mn5, ASTM LCC, UNS J02505, ISO G17Mn5, ASTM A352 Grade LCC, ASTM Grade LCC, ASTM A757 Grade A1Q, ASTM A1Q, ASTM Grade A1Q, UNS J03002, DIN 1.1131, DIN G17Mn5, AFNOR G17Mn5, BS G17Mn5, EN 1.1131
EN 10213 Grade G17Mn5 quenched and tempered (+QT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.8 g/cm³ |
EN 10213 Grade G17Mn5 quenched and tempered (+QT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.38E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.5E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Max service temperature, long |
- |
Max service temperature, long of -120 - 300 °C |
- |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 460 J/(kg·K) |
- |
| Thermal conductivity |
50.0 °C |
Thermal conductivity of 45 W/(m·K) |
- |
EN 10213 Grade G17Mn5 quenched and tempered (+QT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.15 - 0.2 % |
| Chromium |
Chromium of 0.3 % |
| Copper |
Copper of 0.3 % |
| Manganese |
Manganese of 1 - 1.6 % |
| Molybdenum |
Molybdenum of 0.12 % |
| Nickel |
Nickel of 0.4 % |
| Phosphorus |
Phosphorus of 0.02 % |
| Silicon |
Silicon of 0.6 % |
| Sulfur |
Sulfur of 0.02 % |
| Vanadium |
Vanadium of 0.03 % |
EN 10213 Grade G17Mn5 quenched and tempered (+QT) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10213 Grade G17Mn5 quenched and tempered (+QT) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
EN 10213 Grade G17Mn5 quenched and tempered (+QT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation |
20.0 °C |
Elongation of 24 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 450 - 600 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 240 MPa |
- |
Experience the seamless integration of our steel products into your projects, delivering flawless results every time.