DIN 17182 Grade G17Mn5 normalized or normalized formed (+N)
DIN 17182 Grade G17Mn5 normalized or normalized formed (+N) introduction
In comparison to the unalloyed cast steel grades according to DIN 1681, the materials of this group show distinctly higher values of the notch impact energy. As a result of their low carbon content (0.23 per cent maximum), they are well suitable for welding.
Equivalent material: DIN 1.1131, DIN GS-16Mn5, AFNOR G17Mn5, BS G17Mn5, EN G17Mn5, EN 1.1131, ISO G17Mn5, UNS J02505, UNS J03002
DIN 17182 Grade G17Mn5 normalized or normalized formed (+N) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
DIN 17182 Grade G17Mn5 normalized or normalized formed (+N) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Max service temperature, long |
- |
Max service temperature, long of -120 - 300 °C |
- |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
DIN 17182 Grade G17Mn5 normalized or normalized formed (+N) chemical
| Property |
Value |
| Carbon |
Carbon of 0.15 - 0.2 % |
| Chromium |
Chromium of 0.3 % |
| Manganese |
Manganese of 1 - 1.5 % |
| Molybdenum |
Molybdenum of 0.15 % |
| Nickel |
Nickel of 0.4 % |
| Phosphorus |
Phosphorus of 0.02 % |
| Silicon |
Silicon of 0.6 % |
| Sulfur |
Sulfur of 0.015 % |
DIN 17182 Grade G17Mn5 normalized or normalized formed (+N) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
DIN 17182 Grade G17Mn5 normalized or normalized formed (+N) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
DIN 17182 Grade G17Mn5 normalized or normalized formed (+N) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation |
20.0 °C |
Elongation of 25 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 430 - 600 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 230 - 260 MPa |
- |
Unlock the potential of your projects and drive success with our high-performance steel.