EN 10130 Grade DC06 skin passed
EN 10130 Grade DC06 skin passed introduction
The non-alloy steel DC06 (IF 18) is suitable for highest deformation demands and complex cold formed construction components. Products made of DC06 do not show any stretcher strains.
Welding:
DC06 is weldable by the following welding methods: MAG (metal-active-gas), plasma welding, laser welding, compression weld welding, resistance welding (spot, roll weld, buckle welding), arc welding.
The steel acts as substrate for surface refined and coated bands and sheets.
Application of DC06: construction trade, car manufacturing, traffic system.
Acc. to DIN EN 10139 DC06 is offered as cold rolled band or bar, cut in strength range HK270.
Equivalent material: ASTM CSTypeA.BorC, DIN IF18, GB DC06, IS CR5, IS SPCG, ASTM A1008EDDS, ASTM EDDS, DIN 1.0873, EN 1.0873, DIN DC06, EN HX260YD, AFNOR DC06, AFNOR IF, BS DC06, JIS SPCG, JIS SECG, ISO CR5, ISO T005, ISO 05, GB/T LT05, GB/T U43016, GB/T DC06
EN 10130 Grade DC06 skin passed general
| Property |
Temperature |
Value |
Condition |
Related Standards |
Shape |
| Density |
20 °C |
Density of 7.85 g/cm³ |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
EN 10130 Grade DC06 skin passed thermal
| Property |
Temperature |
Value |
Condition |
Related Standards |
Shape |
Comment |
| Coefficient of thermal expansion |
-100 °C |
Coefficient of thermal expansion of 1.08e-05 1/K |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
20 °C |
Coefficient of thermal expansion of 1.19e-05 1/K |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
100 °C |
Coefficient of thermal expansion of 1.25e-05 1/K |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
200 °C |
Coefficient of thermal expansion of 1.3e-05 1/K |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
300 °C |
Coefficient of thermal expansion of 1.36e-05 1/K |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
400 °C |
Coefficient of thermal expansion of 1.41e-05 1/K |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
500 °C |
Coefficient of thermal expansion of 1.45e-05 1/K |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
600 °C |
Coefficient of thermal expansion of 1.49e-05 1/K |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| Max service temperature |
- |
Max service temperature of 383.1 °C |
- |
- |
- |
Predicted Value, Long |
| - |
- |
Max service temperature of 500 °C |
- |
- |
- |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
- |
- |
- |
Typical for Low Carbon Steel |
| Specific heat capacity |
-100 °C |
Specific heat capacity of 423 J/(kg·K) |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
20 °C |
Specific heat capacity of 461 J/(kg·K) |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
100 °C |
Specific heat capacity of 479 J/(kg·K) |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
200 °C |
Specific heat capacity of 499 J/(kg·K) |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
300 °C |
Specific heat capacity of 517 J/(kg·K) |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
400 °C |
Specific heat capacity of 536 J/(kg·K) |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
500 °C |
Specific heat capacity of 558 J/(kg·K) |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
600 °C |
Specific heat capacity of 587 J/(kg·K) |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| Thermal conductivity |
20 °C |
Thermal conductivity of 57.5 W/(m·K) |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
100 °C |
Thermal conductivity of 55.7 W/(m·K) |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
200 °C |
Thermal conductivity of 51.9 W/(m·K) |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
300 °C |
Thermal conductivity of 47.6 W/(m·K) |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
400 °C |
Thermal conductivity of 43.4 W/(m·K) |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
500 °C |
Thermal conductivity of 39.6 W/(m·K) |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
600 °C |
Thermal conductivity of 36 W/(m·K) |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| Thermal diffusivity |
20 °C |
Thermal diffusivity of 15.9 mm²/s |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
100 °C |
Thermal diffusivity of 14.3 mm²/s |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
200 °C |
Thermal diffusivity of 12.5 mm²/s |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
300 °C |
Thermal diffusivity of 10.8 mm²/s |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
400 °C |
Thermal diffusivity of 9.2 mm²/s |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
500 °C |
Thermal diffusivity of 7.6 mm²/s |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
600 °C |
Thermal diffusivity of 6.1 mm²/s |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
EN 10130 Grade DC06 skin passed chemical
| Property |
Value |
Condition |
Related Standards |
Shape |
| Carbon |
Carbon of 0.02 % |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
| Manganese |
Manganese of 0.25 % |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
| Phosphorus |
Phosphorus of 0.02 % |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
| Sulfur |
Sulfur of 0.02 % |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
| Titanium |
Titanium of 0.3 % |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
EN 10130 Grade DC06 skin passed magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10130 Grade DC06 skin passed electrical
| Property |
Temperature |
Value |
Condition |
Related Standards |
Shape |
Comment |
| Electrical conductivity |
- |
Electrical conductivity of 8 S/m |
- |
- |
- |
Predicted Value |
| Electrical resistivity |
20 °C |
Electrical resistivity of 1.1e-07 Ω·m |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
100 °C |
Electrical resistivity of 2.3e-07 Ω·m |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
200 °C |
Electrical resistivity of 3.04e-07 Ω·m |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
300 °C |
Electrical resistivity of 3.94e-07 Ω·m |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
400 °C |
Electrical resistivity of 5.01e-07 Ω·m |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
500 °C |
Electrical resistivity of 6.25e-07 Ω·m |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
600 °C |
Electrical resistivity of 7.7e-07 Ω·m |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
EN 10130 Grade DC06 skin passed mechanical
| Property |
Temperature |
Value |
Condition |
Related Standards |
Shape |
Comment |
| Elastic modulus |
-100 °C |
Elastic modulus of 217 GPa |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
20 °C |
Elastic modulus of 212 GPa |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
100 °C |
Elastic modulus of 207 GPa |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
200 °C |
Elastic modulus of 199 GPa |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
300 °C |
Elastic modulus of 192 GPa |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
400 °C |
Elastic modulus of 184 GPa |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
500 °C |
Elastic modulus of 175 GPa |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
600 °C |
Elastic modulus of 164 GPa |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| Elongation |
- |
Elongation of 18.6 % |
- |
- |
- |
Predicted Value, Transverse |
| - |
- |
Elongation of 20.2 % |
- |
- |
- |
Predicted Value, A200 |
| - |
- |
Elongation of 22.3 % |
- |
- |
- |
Predicted Value, A5 |
| - |
- |
Elongation of 22.5 % |
- |
- |
- |
Predicted Value, A80 Transverse |
| - |
- |
Elongation of 37.2 % |
- |
- |
- |
Predicted Value |
| - |
- |
Elongation of 39.4 % |
- |
- |
- |
Predicted Value, A50 |
| - |
20 °C |
Elongation of 38 % |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
A80 |
| - |
20 °C |
Elongation of 41 % |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
A80 |
| Hardness, Brinell |
- |
Hardness, Brinell of 272 [-] |
- |
- |
- |
Predicted Value, Transverse |
| Poisson's ratio |
20 °C |
Poisson's ratio of 0.284 [-] |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| Reduction of area |
- |
Reduction of area of 42.9 % |
- |
- |
- |
Predicted Value, Transverse |
| - |
- |
Reduction of area of 47.3 % |
- |
- |
- |
Predicted Value |
| Shear modulus |
- |
Shear modulus of 82 GPa |
- |
- |
- |
Typical for Low Carbon Steel |
| Shear strength |
- |
Shear strength of 544.1 MPa |
- |
- |
- |
Predicted Value |
| Tensile strength |
20 °C |
Tensile strength of 270 - 350 MPa |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
20 °C |
Tensile strength of 270 - 330 MPa |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| Yield strength |
- |
Yield strength of 280.5 MPa |
- |
- |
- |
Predicted Value, RP1 |
| - |
- |
Yield strength of 280.5 MPa |
- |
- |
- |
Predicted Value, Transverse |
| - |
- |
Yield strength of 317.2 MPa |
- |
- |
- |
Predicted Value, RP1 Transverse |
| - |
- |
Yield strength of 318.5 MPa |
- |
- |
- |
Predicted Value, RP05 |
| - |
- |
Yield strength of 323.2 MPa |
- |
- |
- |
Predicted Value, RP02 |
| - |
- |
Yield strength of 478.6 MPa |
- |
- |
- |
Predicted Value, RP02 Transverse |
| - |
- |
Yield strength of 494.9 MPa |
- |
- |
- |
Predicted Value, RP002 |
| - |
20 °C |
Yield strength of 120 - 180 MPa |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| - |
20 °C |
Yield strength of 120 - 170 MPa |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
Increase productivity and maximize results with our efficient steel solutions.
-- Our promise
Similar or equivalent steel materials
Get a quote