EN 10130 Grade DC05 skin passed
EN 10130 Grade DC05 skin passed introduction
The non-alloy steel DC05 acc. to DIN EN 10130 is as a special deep drawing quality suitable for cold forming of complexest profile forms, construction components and molded parts. To freedom of stretcher strains applies a period of 6 months after provision of the products for surface type A and B.
Welding:
DC05 is weldable by the following welding methods: MAG (metal-active-gas), plasma welding, laser welding, compression weld welding, resistance welding (spot, roll weld, buckle welding), arc welding.
The steel acts as substrate for surface refined and coated bands and sheets.
Application of DC05: construction trade, car manufacturing, traffic system.
Acc. to DIN EN 10139 DC05 is offered as cold rolled band or bar, cut in strength range HK270.
Equivalent material: ASTM CSTypeA.BorC, GB DC05, IS CR5, IS CR4, IS SPCF, IS SPCE, DIN St15, DIN 1.0312, EN 1.0312, DIN St 15, DIN DC05, AFNOR DC05, BS DC05, JIS SPCF, JIS SPCE, JIS CR4, ISO CR4, ISO 04, ISO HR4
EN 10130 Grade DC05 skin passed general
| Property |
Value |
Comment |
| Density |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10130 Grade DC05 skin passed thermal
| Property |
Value |
Comment |
| Coefficient of thermal expansion |
Coefficient of thermal expansion of 1.32e-05 - 1.38e-05 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
Max service temperature of 323.8 °C |
Predicted Value, Long |
| - |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
EN 10130 Grade DC05 skin passed chemical
| Property |
Value |
Condition |
Related Standards |
Shape |
| Carbon |
Carbon of 0.06 % |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
| Manganese |
Manganese of 0.35 % |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
| Phosphorus |
Phosphorus of 0.025 % |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
| Sulfur |
Sulfur of 0.025 % |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
EN 10130 Grade DC05 skin passed magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10130 Grade DC05 skin passed electrical
| Property |
Value |
Comment |
| Electrical conductivity |
Electrical conductivity of 8 S/m |
Predicted Value |
| Electrical resistivity |
Electrical resistivity of 1.43e-07 - 1.74e-07 Ω·m |
Typical for Carbon Steel |
EN 10130 Grade DC05 skin passed mechanical
| Property |
Temperature |
Value |
Condition |
Related Standards |
Shape |
Comment |
| Elastic modulus |
- |
Elastic modulus of 200 - 215 GPa |
- |
- |
- |
Typical for Low Carbon Steel |
| Elongation |
- |
Elongation of 19.9 % |
- |
- |
- |
Predicted Value, Transverse |
| - |
- |
Elongation of 20.6 % |
- |
- |
- |
Predicted Value, A200 |
| - |
- |
Elongation of 21.4 % |
- |
- |
- |
Predicted Value, A5 |
| - |
- |
Elongation of 24.1 % |
- |
- |
- |
Predicted Value, A80 Transverse |
| - |
- |
Elongation of 37.5 % |
- |
- |
- |
Predicted Value |
| - |
- |
Elongation of 37.7 % |
- |
- |
- |
Predicted Value, A50 |
| - |
20 °C |
Elongation of 40 % |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
A80 |
| Hardness, Brinell |
- |
Hardness, Brinell of 267 [-] |
- |
- |
- |
Predicted Value, Transverse |
| Poisson's ratio |
- |
Poisson's ratio of 0.29 [-] |
- |
- |
- |
Typical for Low Carbon Steel |
| Reduction of area |
- |
Reduction of area of 43.2 % |
- |
- |
- |
Predicted Value, Transverse |
| - |
- |
Reduction of area of 45.5 % |
- |
- |
- |
Predicted Value |
| Shear modulus |
- |
Shear modulus of 82 GPa |
- |
- |
- |
Typical for Low Carbon Steel |
| Shear strength |
- |
Shear strength of 565.7 MPa |
- |
- |
- |
Predicted Value |
| Tensile strength |
20 °C |
Tensile strength of 270 - 330 MPa |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |
| Yield strength |
- |
Yield strength of 256.6 MPa |
- |
- |
- |
Predicted Value, RP1 |
| - |
- |
Yield strength of 263.8 MPa |
- |
- |
- |
Predicted Value, RP05 |
| - |
- |
Yield strength of 288.4 MPa |
- |
- |
- |
Predicted Value, Transverse |
| - |
- |
Yield strength of 314 MPa |
- |
- |
- |
Predicted Value, RP02 |
| - |
- |
Yield strength of 315.1 MPa |
- |
- |
- |
Predicted Value, RP1 Transverse |
| - |
- |
Yield strength of 453 MPa |
- |
- |
- |
Predicted Value, RP02 Transverse |
| - |
- |
Yield strength of 489.2 MPa |
- |
- |
- |
Predicted Value, RP002 |
| - |
20 °C |
Yield strength of 140 - 180 MPa |
skin passed |
EN 10130 |
Sheet, Flat, Bar, Strip |
- |