EN 10084 Grade 17Cr3 quenched (+Q)
EN 10084 Grade 17Cr3 quenched (+Q) introduction
Steel 17Cr3 is suitable for parts of lower dimension in vehicle manufacturing and machine engineering requiring a high wear resistance (e.g. camshafts, piston bolts, cylinder).
Equivalent material: GB 15CrH, GB A20155, EN 1.7016, IS 15Cr3(-S), ISO 17Cr3, ASTM A434 Grade 5115, UNS G51150, UNS G51170, SAE 5115, SAE 5117, DIN 1.7016, DIN 17Cr3, AFNOR 17Cr3, BS 17Cr3, AISI 6118H, AISI 6118, SAE 6118H, SAE 6118, JIS SCr415H, JIS SCr415, GOST 15ChA, GB/T 15CrA, GB/T 15CrH, GB/T A20155, ASTM 6118, UNS H61180, UNS G46150, UNS G61180
EN 10084 Grade 17Cr3 quenched (+Q) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.82 - 7.85 g/cm³ |
EN 10084 Grade 17Cr3 quenched (+Q) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.1E-5 - 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.12E-5 - 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.25E-5 - 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 460 - 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 - 480 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 - 520 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 39.6 - 44 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 41 - 41.9 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 39.8 - 41 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 39.9 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 38.1 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 35.9 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 33.6 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 11 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 10.6 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 9.9 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 9 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.1 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 6.9 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 5.7 mm²/s |
- |
EN 10084 Grade 17Cr3 quenched (+Q) chemical
| Property |
Value |
| Carbon |
Carbon of 0.14 - 0.2 % |
| Chromium |
Chromium of 0.7 - 1 % |
| Copper |
Copper of 0.4 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
EN 10084 Grade 17Cr3 quenched (+Q) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.6E-7 - 2.63E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 3.12E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.85E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.7E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.71E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.88E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 8.25E-7 Ω·m |
EN 10084 Grade 17Cr3 quenched (+Q) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 210 - 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 195 - 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 185 - 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 600 - 800 MPa |
- |
Unlock the potential of your projects and drive success with our high-performance steel.
-- Our promise
Similar or equivalent steel materials