ISO 683-3 Grade 16MnCr5 normalized or normalized formed (+N)
ISO 683-3 Grade 16MnCr5 normalized or normalized formed (+N) introduction
Steel 16 MnCr5 is suitable for parts of higher dimension in vehicle manufacturing and machine engineering, requiring higher core strength and favorable ductility properties (gear wheels, shafts, steering parts).
Equivalent material: GB 16CrMnH, GB A22165, EN 1.7131, IS 16Mn5Cr4, IS 16MnCr5, GOST 18ChG, GOST 18ХГ, ASTM A434 Grade 5115, UNS G51150, SAE 5115, GB 15CrMn, GB A22152, GB 20CrMn, GB A22202, GB 20CrMnH, GB 20CrMnAH, GB A22205, GB A22207, DIN 1.7131, DIN 16MnCr5, AFNOR 16MC5, BS 527M20, UNI 16MnCr5, SS 2511, UNE 16MnCr5, AISI PS59, AISI PS64, AISI PS65, AISI 5115, SAE PS59, SAE PS64, SAE PS65, JIS SCR415, ASTM 5115
ISO 683-3 Grade 16MnCr5 normalized or normalized formed (+N) general
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
| Density | 20 °C | Density of 7.85 g/cm³ | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire |
ISO 683-3 Grade 16MnCr5 normalized or normalized formed (+N) thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Coefficient of thermal expansion | -100 °C | Coefficient of thermal expansion of 1.05e-05 1/K | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 20 °C | Coefficient of thermal expansion of 1.15e-05 1/K | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 100 °C | Coefficient of thermal expansion of 1.1e-05 - 1.21e-05 1/K | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 100 °C | Coefficient of thermal expansion of 1.1e-05 1/K | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 100 °C | Coefficient of thermal expansion of 1.21e-05 1/K | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 200 °C | Coefficient of thermal expansion of 1.27e-05 1/K | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 300 °C | Coefficient of thermal expansion of 1.32e-05 1/K | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 400 °C | Coefficient of thermal expansion of 1.36e-05 1/K | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 500 °C | Coefficient of thermal expansion of 1.4e-05 1/K | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 600 °C | Coefficient of thermal expansion of 1.44e-05 1/K | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| Melting point | - | Melting point of 1382 - 1529 °C | - | - | - | Typical for Chromium Steel |
| Specific heat capacity | -100 °C | Specific heat capacity of 423 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 20 °C | Specific heat capacity of 460 - 461 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 20 °C | Specific heat capacity of 460 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 20 °C | Specific heat capacity of 461 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 100 °C | Specific heat capacity of 479 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 200 °C | Specific heat capacity of 499 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 300 °C | Specific heat capacity of 517 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 400 °C | Specific heat capacity of 536 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 500 °C | Specific heat capacity of 558 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 600 °C | Specific heat capacity of 587 J/(kg·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| Thermal conductivity | 20 °C | Thermal conductivity of 42 - 45.9 W/(m·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 20 °C | Thermal conductivity of 42 W/(m·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 20 °C | Thermal conductivity of 45.9 W/(m·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 100 °C | Thermal conductivity of 39.8 - 46.4 W/(m·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 100 °C | Thermal conductivity of 39.8 W/(m·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 100 °C | Thermal conductivity of 46.4 W/(m·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 200 °C | Thermal conductivity of 37.7 - 45.6 W/(m·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 200 °C | Thermal conductivity of 37.7 W/(m·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 200 °C | Thermal conductivity of 45.6 W/(m·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 300 °C | Thermal conductivity of 43.5 W/(m·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 400 °C | Thermal conductivity of 40.9 W/(m·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 500 °C | Thermal conductivity of 38.2 W/(m·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 600 °C | Thermal conductivity of 35.5 W/(m·K) | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| Thermal diffusivity | 20 °C | Thermal diffusivity of 12.7 mm²/s | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 100 °C | Thermal diffusivity of 12 mm²/s | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 200 °C | Thermal diffusivity of 11 mm²/s | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 300 °C | Thermal diffusivity of 9.9 mm²/s | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 400 °C | Thermal diffusivity of 8.7 mm²/s | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 500 °C | Thermal diffusivity of 7.3 mm²/s | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 600 °C | Thermal diffusivity of 6 mm²/s | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
ISO 683-3 Grade 16MnCr5 normalized or normalized formed (+N) chemical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Carbon | Carbon of 0.14 - 0.19 % | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire |
| Chromium | Chromium of 0.8 - 1.1 % | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire |
| Copper | Copper of 0.4 % | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire |
| Manganese | Manganese of 1 - 1.3 % | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire |
| Phosphorus | Phosphorus of 0.025 % | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire |
| Silicon | Silicon of 0.15 - 0.4 % | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire |
| - | Silicon of 0.4 % | normalized or normalized formed (+N) | EN 10084, ISO 683-3 | Bar, Flat, Forging, Wire |
| Sulfur | Sulfur of 0.035 % | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire |
ISO 683-3 Grade 16MnCr5 normalized or normalized formed (+N) electrical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Electrical conductivity | - | Electrical conductivity of 4 S/m | - | - | - | Predicted Value |
| Electrical resistivity | 20 °C | Electrical resistivity of 1.6e-07 - 2.27e-07 Ω·m | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 20 °C | Electrical resistivity of 1.6e-07 Ω·m | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 20 °C | Electrical resistivity of 2.27e-07 Ω·m | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 100 °C | Electrical resistivity of 2.76e-07 Ω·m | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 200 °C | Electrical resistivity of 3.46e-07 Ω·m | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 300 °C | Electrical resistivity of 4.31e-07 Ω·m | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 400 °C | Electrical resistivity of 5.32e-07 Ω·m | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 500 °C | Electrical resistivity of 6.48e-07 Ω·m | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 600 °C | Electrical resistivity of 7.81e-07 Ω·m | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
ISO 683-3 Grade 16MnCr5 normalized or normalized formed (+N) mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Elastic modulus | -100 °C | Elastic modulus of 217 GPa | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 20 °C | Elastic modulus of 210 - 212 GPa | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 20 °C | Elastic modulus of 210 GPa | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 20 °C | Elastic modulus of 212 GPa | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 100 °C | Elastic modulus of 207 GPa | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 200 °C | Elastic modulus of 188 - 199 GPa | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 200 °C | Elastic modulus of 188 GPa | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 200 °C | Elastic modulus of 199 GPa | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 300 °C | Elastic modulus of 192 GPa | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 400 °C | Elastic modulus of 184 GPa | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 500 °C | Elastic modulus of 175 GPa | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| - | 600 °C | Elastic modulus of 164 GPa | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| Elongation | - | Elongation of 14.7 % | - | - | - | Predicted Value, A80 |
| - | - | Elongation of 15.5 % | - | - | - | Predicted Value, A200 |
| - | - | Elongation of 16.5 % | - | - | - | Predicted Value, Transverse |
| - | - | Elongation of 17.8 % | - | - | - | Predicted Value, A50 |
| - | - | Elongation of 17.8 % | - | - | - | Predicted Value, A80 Transverse |
| - | - | Elongation of 18.4 % | - | - | - | Predicted Value, A5 |
| - | - | Elongation of 20.9 % | - | - | - | Predicted Value |
| Poisson's ratio | 20 °C | Poisson's ratio of 0.284 [-] | normalized or normalized formed (+N) | EN 10084, ISO 683-3 | Bar, Flat, Forging, Wire | - |
| Reduction of area | - | Reduction of area of 41.4 % | - | - | - | Predicted Value, Transverse |
| - | - | Reduction of area of 47.2 % | - | - | - | Predicted Value |
| Shear modulus | 20 °C | Shear modulus of 81 GPa | normalized or normalized formed (+N) | ISO 683-3, EN 10084 | Bar, Flat, Forging, Wire | - |
| Shear strength | - | Shear strength of 514.2 MPa | - | - | - | Predicted Value |
Withstand challenging environments and harsh conditions with our durable steel materials.
-- Our promise
Similar or equivalent steel materials
- EN 10132-2 Grade 16MnCr5 soft annealed or soft annealed and skin passed (+A or +A+LC)
- EN 10132-2 Grade 17Cr3 soft annealed or soft annealed and skin passed (+A or +A+LC)
- EN 10263-3 Grade 16MnCr5 annealed to achieve spheroidized carbides (+AC)
- EN 10263-3 Grade 16MnCr5 annealed to achieve spheroidized carbides and turned
- EN 10263-3 Grade 16MnCr5 cold drawn, annealed to achieve spheroidized carbides and slightly skin passed
- EN 10263-3 Grade 17Cr3 annealed to achieve spheroidized carbides (+AC)
- EN 10263-3 Grade 17Cr3 annealed to achieve spheroidized carbides and turned
- EN 10263-3 Grade 17Cr3 cold drawn, annealed to achieve spheroidized carbides and slightly skin passed
- DIN 1652-3 Grade 16MnCr5 treated to ferritic-pearlite structure and cold-drawn
- DIN 1652-3 Grade 16MnCr5 cold drawn