EN 10132-2 Grade 16MnCr5 soft annealed or soft annealed and skin passed (+A or +A+LC)
EN 10132-2 Grade 16MnCr5 soft annealed or soft annealed and skin passed (+A or +A+LC) introduction
Cold-rolled narrow strip made of the alloy steel 16MnCr5 will be delivered in thicknesses up to 10 mm for case hardening in following conditions:
- soft annealed or soft annealed and little rerolled (+A or +LC),
- cold rolled (+CR).
Equivalent material: GB 16CrMnH, GB A22165, IS 16Mn5Cr4, ISO 16MnCr5, ASTM A506 Grade 5115, ASTM Grade 5115, SAE 5115, UNS G51150, DIN 1.7131, DIN 16MnCr5, AFNOR 16MC5, BS 527M20, UNI 16MnCr5, SS 2511, UNE 16MnCr5, AISI PS59, AISI PS64, AISI PS65, AISI 5115, SAE PS59, SAE PS64, SAE PS65, JIS SCR415, EN 1.7131, ASTM 5115
EN 10132-2 Grade 16MnCr5 soft annealed or soft annealed and skin passed (+A or +A+LC) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
EN 10132-2 Grade 16MnCr5 soft annealed or soft annealed and skin passed (+A or +A+LC) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.05E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.15E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.21E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.27E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.4E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.44E-5 1/K |
- |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 45.9 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 46.4 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 45.6 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 43.5 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 40.9 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 38.2 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 35.5 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 12.7 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 12 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 11 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 9.9 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.7 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.3 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 6 mm²/s |
- |
EN 10132-2 Grade 16MnCr5 soft annealed or soft annealed and skin passed (+A or +A+LC) chemical
| Property |
Value |
| Carbon |
Carbon of 0.14 - 0.19 % |
| Chromium |
Chromium of 0.8 - 1.1 % |
| Manganese |
Manganese of 1 - 1.3 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
EN 10132-2 Grade 16MnCr5 soft annealed or soft annealed and skin passed (+A or +A+LC) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 2.27E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.76E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.46E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.31E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.32E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.48E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 7.81E-7 Ω·m |
EN 10132-2 Grade 16MnCr5 soft annealed or soft annealed and skin passed (+A or +A+LC) mechanical
| Property |
Temperature |
Value |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
| - |
20.0 °C |
Elastic modulus of 212 GPa |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
| - |
200.0 °C |
Elastic modulus of 199 GPa |
| - |
300.0 °C |
Elastic modulus of 192 GPa |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
| Elongation A80 |
20.0 °C |
Elongation A80 of 21 % |
| Hardness, Rockwell B |
20.0 °C |
Hardness, Rockwell B of 84 [-] |
| Hardness, Vickers |
20.0 °C |
Hardness, Vickers of 170 [-] |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.28 [-] |
| Tensile strength |
20.0 °C |
Tensile strength of 550 MPa |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 420 MPa |