DIN 5512-2 Grade St14
Equivalent material: EN DC 04, DIN 1.0335, DIN 1.0338, EN FeP04, AFNOR ES, JIS SPCE, UNI FeP04, UNE AP04, SS1147, PN 08J, GOST 05kp, GOST 08kp, GOST 08YU, ISO CR04, ISO CR24, DIN 1.0338, DIN St 14, DIN St 4, DIN DC04, AFNOR ES, AFNOR DC04, BS 1CR, BS 1CS, BS 1HR, BS 1HS, BS CR1, BS DC04, UNI FeP04, UNE AP04, JIS SPCE, JIS SPCF, JIS CR3, EN DC04, EN FeP04, EN DC04, EN 1.0338, ISO CR3, ISO CR24, GOST 08JuA, GB/T 08F, GB/T U20080
DIN 5512-2 Grade St14 general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.86 g/cm³ |
DIN 5512-2 Grade St14 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1400 - 1500 °C |
- |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 45 W/(m·K) |
- |
DIN 5512-2 Grade St14 chemical
| Property |
Value |
| Carbon |
Carbon of 0.08 % |
| Manganese |
Manganese of 0.4 % |
| Nickel |
Nickel of 0.03 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.01 % |
| Sulfur |
Sulfur of 0.03 % |
DIN 5512-2 Grade St14 magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
DIN 5512-2 Grade St14 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
DIN 5512-2 Grade St14 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 180 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 36 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 270 - 350 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 220 MPa |
- |