DIN 1652-3 Grade 17Cr3 cold drawn or turned and soft annealed
DIN 1652-3 Grade 17Cr3 cold drawn or turned and soft annealed introduction
The steel 17 Cr 3 is used for high wear loaded smaller parts in the vehicle and mechanical engineering (e.g. camshafts, piston pins, cylinder).
The lowest application amounts to -25 °C, the best application up to 25 mm nominal size.
Equivalent material: GB 15Cr, BS 523M15, GOST 15Ch, PN 15HN, ASTM 4615, DIN 1.7016, AFNOR 17Cr3, BS 17Cr3, AISI 6118H, AISI 6118, SAE 6118H, SAE 6118, JIS SCr415H, JIS SCr415, EN 17Cr3, EN 1.7016, ISO 17Cr3, GOST 15ChA, GB/T 15CrA, GB/T 15CrH, GB/T A20155, ASTM 6118, UNS H61180, UNS G46150, UNS G61180
DIN 1652-3 Grade 17Cr3 cold drawn or turned and soft annealed general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.82 g/cm³ |
DIN 1652-3 Grade 17Cr3 cold drawn or turned and soft annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Max service temperature, long |
- |
Max service temperature, long of -25 - 0 °C |
- |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 39.6 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 41 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 41 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 39.9 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 38.1 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 35.9 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 33.6 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 11 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 10.6 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 9.9 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 9 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.1 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 6.9 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 5.7 mm²/s |
- |
DIN 1652-3 Grade 17Cr3 cold drawn or turned and soft annealed chemical
| Property |
Value |
| Carbon |
Carbon of 0.14 - 0.2 % |
| Chromium |
Chromium of 0.6 - 0.9 % |
| Manganese |
Manganese of 0.4 - 0.7 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
DIN 1652-3 Grade 17Cr3 cold drawn or turned and soft annealed electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 2.63E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 3.12E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.85E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.7E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.71E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.88E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 8.25E-7 Ω·m |
DIN 1652-3 Grade 17Cr3 cold drawn or turned and soft annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 174 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Steel |