ASTM A209 Grade T1 Heat-Treated
Equivalent material: DIN 1.5423, DIN 16Mo5, BS 1503-245-420, UNI 16Mo5, UNE 16Mo5, AISI 4520, SAE 4520, JIS SB450M, JIS SB480, JIS SB480M, JIS STBA12, JIS STBA13, JIS SB49M, EN 1.5423, ASTM Grade F1
ASTM A209 Grade T1 Heat-Treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Molybdenum Steel |
ASTM A209 Grade T1 Heat-Treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.29E-5 1/K |
Typical for Molybdenum Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Molybdenum Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 456 J/(kg·K) |
Typical for Molybdenum Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 37 - 48 W/(m·K) |
Typical for Molybdenum Steel |
ASTM A209 Grade T1 Heat-Treated chemical
| Property |
Value |
| Carbon |
Carbon of 0.1 - 0.2 % |
| Manganese |
Manganese of 0.3 - 0.8 % |
| Molybdenum |
Molybdenum of 0.44 - 0.65 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.1 - 0.5 % |
| Sulfur |
Sulfur of 0.025 % |
ASTM A209 Grade T1 Heat-Treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Molybdenum Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 30 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 146 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 80 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Molybdenum Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 380 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 205 MPa |
- |