EN 10028-2 Grade 16Mo3 normalized or normalized formed (+N)

Home
Material
EN 10028-2 Grade 16Mo3 normalized or normalized formed (+N)

EN 10028-2 Grade 16Mo3 normalized or normalized formed (+N)

EN 10028-2 Grade 16Mo3 normalized or normalized formed (+N) introduction

Heat-resistant alloy high-grade steel for application in pressure vessel and apparatus construction.
For permanent operating applicable up to approx. 530 °C.

Equivalent material: IS 16Mo3H, IS SB49M, ASTM A204 Grade A, ASTM A204 Grade B, ASTM A204 Grade C, UNS K11820, UNS K12020, UNS K12320, DIN 16Mo3, DIN 1.5415, AS 15Mo3KK, NBN 16Mo3, AFNOR NFA36-206, UNI 16Mo3, PN 16M, SS 2912, ASTM Grade A, DIN 15Mo3, IS 16Mo3, EN 1.5415, AFNOR 16Mo3, AFNOR 15D3, BS 16Mo3, JIS STBA12, JIS STPA12, JIS STFA12, ISO 16Mo3, ISO F26, ASTM Grade F1, DIN 1.5417, EN 1.5417, DIN 26Mo2, EN 15Mo3, AFNOR TU 15 03, AFNOR 15 D3, UNI 16Mo3KW, UNE 16Mo3, BS 1501-240, BS 243, JIS SB480, JIS SB480M

EN 10028-2 Grade 16Mo3 normalized or normalized formed (+N) general

Property	Temperature	Value	Condition	Related Standards	Shape
Density	20 °C	Density of 7.848 - 7.85 g/cm³	normalized or normalized formed (+N)	EN 10028-2	Flat
-	20 °C	Density of 7.848 - 7.86 g/cm³	normalized or normalized formed (+N)	EN 10028-2	Flat
-	20 °C	Density of 7.848 g/cm³	normalized or normalized formed (+N)	EN 10028-2	Flat
-	20 °C	Density of 7.85 g/cm³	normalized or normalized formed (+N)	EN 10028-2	Flat
-	20 °C	Density of 7.85 - 7.86 g/cm³	normalized or normalized formed (+N)	EN 10028-2	Flat
-	20 °C	Density of 7.86 g/cm³	normalized or normalized formed (+N)	EN 10028-2	Sheet, Flat
-	50 °C	Density of 7.839 g/cm³	normalized or normalized formed (+N)	EN 10028-2	Flat
-	100 °C	Density of 7.824 g/cm³	normalized or normalized formed (+N)	EN 10028-2	Flat
-	150 °C	Density of 7.808 g/cm³	normalized or normalized formed (+N)	EN 10028-2	Flat
-	200 °C	Density of 7.792 g/cm³	normalized or normalized formed (+N)	EN 10028-2	Flat
-	250 °C	Density of 7.774 g/cm³	normalized or normalized formed (+N)	EN 10028-2	Flat
-	300 °C	Density of 7.756 g/cm³	normalized or normalized formed (+N)	EN 10028-2	Flat
-	350 °C	Density of 7.738 g/cm³	normalized or normalized formed (+N)	EN 10028-2	Flat
-	400 °C	Density of 7.72 g/cm³	normalized or normalized formed (+N)	EN 10028-2	Flat
-	450 °C	Density of 7.701 g/cm³	normalized or normalized formed (+N)	EN 10028-2	Flat
-	500 °C	Density of 7.682 g/cm³	normalized or normalized formed (+N)	EN 10028-2	Flat
-	550 °C	Density of 7.662 g/cm³	normalized or normalized formed (+N)	EN 10028-2	Flat
-	600 °C	Density of 7.643 g/cm³	normalized or normalized formed (+N)	EN 10028-2	Flat

EN 10028-2 Grade 16Mo3 normalized or normalized formed (+N) thermal

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coefficient of thermal expansion	-100 °C	Coefficient of thermal expansion of 1.05e-05 1/K	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	20 °C	Coefficient of thermal expansion of 1.15e-05 1/K	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	100 °C	Coefficient of thermal expansion of 1.21e-05 - 1.22e-05 1/K	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	100 °C	Coefficient of thermal expansion of 1.21e-05 1/K	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	100 °C	Coefficient of thermal expansion of 1.22e-05 1/K	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	200 °C	Coefficient of thermal expansion of 1.27e-05 - 1.29e-05 1/K	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	200 °C	Coefficient of thermal expansion of 1.27e-05 1/K	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	200 °C	Coefficient of thermal expansion of 1.29e-05 1/K	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	300 °C	Coefficient of thermal expansion of 1.32e-05 - 1.34e-05 1/K	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	300 °C	Coefficient of thermal expansion of 1.32e-05 1/K	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	300 °C	Coefficient of thermal expansion of 1.34e-05 1/K	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	400 °C	Coefficient of thermal expansion of 1.36e-05 - 1.4e-05 1/K	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	400 °C	Coefficient of thermal expansion of 1.36e-05 1/K	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	400 °C	Coefficient of thermal expansion of 1.4e-05 1/K	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	500 °C	Coefficient of thermal expansion of 1.4e-05 1/K	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	500 °C	Coefficient of thermal expansion of 1.4e-05 - 1.43e-05 1/K	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	500 °C	Coefficient of thermal expansion of 1.43e-05 1/K	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	600 °C	Coefficient of thermal expansion of 1.44e-05 - 1.46e-05 1/K	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	600 °C	Coefficient of thermal expansion of 1.44e-05 1/K	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	600 °C	Coefficient of thermal expansion of 1.46e-05 1/K	normalized or normalized formed (+N)	EN 10028-2	Flat	-
Melting point	-	Melting point of 1382 - 1529 °C	-	-	-	Typical for Molybdenum Steel
Specific heat capacity	-100 °C	Specific heat capacity of 423 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	20 °C	Specific heat capacity of 430 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Specific heat capacity of 430 - 461 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Specific heat capacity of 461 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	100 °C	Specific heat capacity of 479 - 500 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	100 °C	Specific heat capacity of 479 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	100 °C	Specific heat capacity of 500 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	200 °C	Specific heat capacity of 499 - 540 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	200 °C	Specific heat capacity of 499 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	200 °C	Specific heat capacity of 540 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	300 °C	Specific heat capacity of 517 - 530 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	300 °C	Specific heat capacity of 517 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	300 °C	Specific heat capacity of 530 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	400 °C	Specific heat capacity of 536 - 620 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	400 °C	Specific heat capacity of 536 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	400 °C	Specific heat capacity of 620 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	500 °C	Specific heat capacity of 558 - 690 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	500 °C	Specific heat capacity of 558 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	500 °C	Specific heat capacity of 690 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	600 °C	Specific heat capacity of 587 - 780 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	600 °C	Specific heat capacity of 587 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	600 °C	Specific heat capacity of 780 J/(kg·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
Thermal conductivity	20 °C	Thermal conductivity of 51 W/(m·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Thermal conductivity of 51 - 52.1 W/(m·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Thermal conductivity of 52.1 W/(m·K)	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	100 °C	Thermal conductivity of 51 W/(m·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	100 °C	Thermal conductivity of 51 - 51.2 W/(m·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	100 °C	Thermal conductivity of 51.2 W/(m·K)	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	200 °C	Thermal conductivity of 48.7 - 49 W/(m·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	200 °C	Thermal conductivity of 48.7 W/(m·K)	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	200 °C	Thermal conductivity of 49 W/(m·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	300 °C	Thermal conductivity of 45 W/(m·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	300 °C	Thermal conductivity of 45 - 45.5 W/(m·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	300 °C	Thermal conductivity of 45.5 W/(m·K)	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	400 °C	Thermal conductivity of 42 W/(m·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	400 °C	Thermal conductivity of 42 - 42.3 W/(m·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	400 °C	Thermal conductivity of 42.3 W/(m·K)	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	500 °C	Thermal conductivity of 39 W/(m·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	500 °C	Thermal conductivity of 39 - 39.1 W/(m·K)	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	500 °C	Thermal conductivity of 39.1 W/(m·K)	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	600 °C	Thermal conductivity of 36 W/(m·K)	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
Thermal diffusivity	20 °C	Thermal diffusivity of 14.4 mm²/s	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	100 °C	Thermal diffusivity of 13.2 mm²/s	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	200 °C	Thermal diffusivity of 11.7 mm²/s	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	300 °C	Thermal diffusivity of 10.3 mm²/s	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	400 °C	Thermal diffusivity of 9 mm²/s	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	500 °C	Thermal diffusivity of 7.5 mm²/s	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	600 °C	Thermal diffusivity of 6 mm²/s	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-

EN 10028-2 Grade 16Mo3 normalized or normalized formed (+N) chemical

Property	Value	Condition	Related Standards	Shape
Carbon	Carbon of 0.12 - 0.2 %	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet
Chromium	Chromium of 0.3 %	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet
Copper	Copper of 0.3 %	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet
Manganese	Manganese of 0.4 - 0.9 %	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet
Molybdenum	Molybdenum of 0.25 - 0.35 %	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet
Nickel	Nickel of 0.3 %	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet
Nitrogen	Nitrogen of 0.012 %	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet
Phosphorus	Phosphorus of 0.025 %	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet
Silicon	Silicon of 0.35 %	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet
Sulfur	Sulfur of 0.01 %	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet

EN 10028-2 Grade 16Mo3 normalized or normalized formed (+N) electrical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Electrical conductivity	-	Electrical conductivity of 5 S/m	-	-	-	Predicted Value
Electrical resistivity	20 °C	Electrical resistivity of 2e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	20 °C	Electrical resistivity of 2e-07 - 2.16e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Electrical resistivity of 2.16e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	50 °C	Electrical resistivity of 2.37e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	100 °C	Electrical resistivity of 2.5e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	100 °C	Electrical resistivity of 2.5e-07 - 2.68e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	100 °C	Electrical resistivity of 2.68e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	150 °C	Electrical resistivity of 3.02e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	200 °C	Electrical resistivity of 3.24e-07 - 3.3e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	200 °C	Electrical resistivity of 3.24e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	200 °C	Electrical resistivity of 3.24e-07 - 3.39e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	200 °C	Electrical resistivity of 3.3e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	200 °C	Electrical resistivity of 3.3e-07 - 3.39e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	200 °C	Electrical resistivity of 3.39e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	250 °C	Electrical resistivity of 3.8e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	300 °C	Electrical resistivity of 4.1e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	300 °C	Electrical resistivity of 4.1e-07 - 4.12e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	300 °C	Electrical resistivity of 4.1e-07 - 4.25e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	300 °C	Electrical resistivity of 4.12e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	300 °C	Electrical resistivity of 4.12e-07 - 4.25e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	300 °C	Electrical resistivity of 4.25e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	350 °C	Electrical resistivity of 4.74e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	400 °C	Electrical resistivity of 5.14e-07 - 5.2e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	400 °C	Electrical resistivity of 5.14e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	400 °C	Electrical resistivity of 5.14e-07 - 5.27e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	400 °C	Electrical resistivity of 5.2e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	400 °C	Electrical resistivity of 5.2e-07 - 5.27e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	400 °C	Electrical resistivity of 5.27e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	450 °C	Electrical resistivity of 5.83e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	500 °C	Electrical resistivity of 6.33e-07 - 6.4e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	500 °C	Electrical resistivity of 6.33e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	500 °C	Electrical resistivity of 6.33e-07 - 6.42e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	500 °C	Electrical resistivity of 6.4e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	500 °C	Electrical resistivity of 6.4e-07 - 6.42e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	500 °C	Electrical resistivity of 6.42e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	550 °C	Electrical resistivity of 7.08e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	600 °C	Electrical resistivity of 7.69e-07 - 7.8e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	600 °C	Electrical resistivity of 7.69e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	600 °C	Electrical resistivity of 7.69e-07 - 7.78e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	600 °C	Electrical resistivity of 7.78e-07 - 7.8e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	600 °C	Electrical resistivity of 7.78e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	600 °C	Electrical resistivity of 7.8e-07 Ω·m	normalized or normalized formed (+N)	EN 10028-2	Flat	-

EN 10028-2 Grade 16Mo3 normalized or normalized formed (+N) mechanical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Elastic modulus	-100 °C	Elastic modulus of 217 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	20 °C	Elastic modulus of 212 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	20 °C	Elastic modulus of 212 - 212.5 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Elastic modulus of 212.5 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	50 °C	Elastic modulus of 211.6 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	100 °C	Elastic modulus of 207 - 208 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	100 °C	Elastic modulus of 207 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	100 °C	Elastic modulus of 207 - 209.2 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	100 °C	Elastic modulus of 208 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	100 °C	Elastic modulus of 208 - 209.2 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	100 °C	Elastic modulus of 209.2 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	150 °C	Elastic modulus of 206.1 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	200 °C	Elastic modulus of 199 - 201 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	200 °C	Elastic modulus of 199 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	200 °C	Elastic modulus of 199 - 202.5 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	200 °C	Elastic modulus of 201 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	200 °C	Elastic modulus of 201 - 202.5 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	200 °C	Elastic modulus of 202.5 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	250 °C	Elastic modulus of 198.4 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	300 °C	Elastic modulus of 192 - 193 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	300 °C	Elastic modulus of 192 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	300 °C	Elastic modulus of 192 - 194.1 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	300 °C	Elastic modulus of 193 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	300 °C	Elastic modulus of 193 - 194.1 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	300 °C	Elastic modulus of 194.1 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	350 °C	Elastic modulus of 189.8 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	400 °C	Elastic modulus of 184 - 185 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	400 °C	Elastic modulus of 184 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	400 °C	Elastic modulus of 184 - 185.5 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	400 °C	Elastic modulus of 185 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	400 °C	Elastic modulus of 185 - 185.5 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	400 °C	Elastic modulus of 185.5 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	450 °C	Elastic modulus of 181.0 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	500 °C	Elastic modulus of 175 - 176 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	500 °C	Elastic modulus of 175 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	500 °C	Elastic modulus of 175 - 176.5 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	500 °C	Elastic modulus of 176 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	500 °C	Elastic modulus of 176 - 176.5 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	500 °C	Elastic modulus of 176.5 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	550 °C	Elastic modulus of 172.0 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	600 °C	Elastic modulus of 164 - 166 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	600 °C	Elastic modulus of 164 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	-
-	600 °C	Elastic modulus of 164 - 167.0 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	600 °C	Elastic modulus of 166 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	600 °C	Elastic modulus of 166 - 167.0 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	600 °C	Elastic modulus of 167.0 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
Elongation	-	Elongation of 17.3 %	-	-	-	Predicted Value, A80 Transverse
-	-	Elongation of 17.8 %	-	-	-	Predicted Value, A80
-	-	Elongation of 18.1 %	-	-	-	Predicted Value, A200
-	-	Elongation of 19.9 %	-	-	-	Predicted Value, A5
-	-	Elongation of 25.8 %	-	-	-	Predicted Value, A50
-	20 °C	Elongation of 22 %	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	Transverse
-	20 °C	Elongation of 22 %	normalized or normalized formed (+N)	EN 10028-2	Flat	-
Hardness, Brinell	-	Hardness, Brinell of 234 [-]	-	-	-	Predicted Value, Transverse
Poisson's ratio	20 °C	Poisson's ratio of 0.286 [-]	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	50 °C	Poisson's ratio of 0.287 [-]	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	100 °C	Poisson's ratio of 0.288 [-]	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	150 °C	Poisson's ratio of 0.289 [-]	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	200 °C	Poisson's ratio of 0.29 [-]	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	250 °C	Poisson's ratio of 0.291 [-]	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	300 °C	Poisson's ratio of 0.293 [-]	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	350 °C	Poisson's ratio of 0.293 [-]	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	400 °C	Poisson's ratio of 0.295 [-]	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	450 °C	Poisson's ratio of 0.297 [-]	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	500 °C	Poisson's ratio of 0.298 [-]	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	550 °C	Poisson's ratio of 0.298 [-]	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	600 °C	Poisson's ratio of 0.297 [-]	normalized or normalized formed (+N)	EN 10028-2	Flat	-
Reduction of area	-	Reduction of area of 43.3 %	-	-	-	Predicted Value
-	-	Reduction of area of 43.4 %	-	-	-	Predicted Value, Transverse
Shear modulus	20 °C	Shear modulus of 82.6 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	50 °C	Shear modulus of 82.2 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	100 °C	Shear modulus of 81.2 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	150 °C	Shear modulus of 80.0 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	200 °C	Shear modulus of 78.5 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	250 °C	Shear modulus of 76.8 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	300 °C	Shear modulus of 75.0 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	350 °C	Shear modulus of 73.4 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	400 °C	Shear modulus of 71.6 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	450 °C	Shear modulus of 69.8 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	500 °C	Shear modulus of 68.0 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	550 °C	Shear modulus of 66.2 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	600 °C	Shear modulus of 64.3 GPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
Shear strength	-	Shear strength of 593 MPa	-	-	-	Predicted Value
Tensile strength	20 °C	Tensile strength of 410 - 590 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	Transverse
-	20 °C	Tensile strength of 410 - 580 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	Transverse
-	20 °C	Tensile strength of 410 - 570 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	Transverse
-	20 °C	Tensile strength of 410 - 590 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Tensile strength of 410 - 580 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Tensile strength of 410 - 570 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Tensile strength of 420 - 590 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	Transverse
-	20 °C	Tensile strength of 420 - 580 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	Transverse
-	20 °C	Tensile strength of 420 - 570 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	Transverse
-	20 °C	Tensile strength of 420 - 590 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Tensile strength of 420 - 580 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Tensile strength of 420 - 570 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Tensile strength of 430 - 590 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	Transverse
-	20 °C	Tensile strength of 430 - 580 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	Transverse
-	20 °C	Tensile strength of 430 - 570 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	Transverse
-	20 °C	Tensile strength of 430 - 590 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Tensile strength of 430 - 580 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Tensile strength of 430 - 570 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Tensile strength of 440 - 590 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	Transverse
-	20 °C	Tensile strength of 440 - 580 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	Transverse
-	20 °C	Tensile strength of 440 - 570 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	Transverse
-	20 °C	Tensile strength of 440 - 590 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Tensile strength of 440 - 580 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Tensile strength of 440 - 570 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
Yield strength	-	Yield strength of 253.1 MPa	-	-	-	Predicted Value, RP1
-	-	Yield strength of 265.3 MPa	-	-	-	Predicted Value, RP1 Transverse
-	-	Yield strength of 336.8 MPa	-	-	-	Predicted Value, RP05
-	-	Yield strength of 345.6 MPa	-	-	-	Predicted Value, RP02 Transverse
-	-	Yield strength of 475.7 MPa	-	-	-	Predicted Value, RP002
-	20 °C	Yield strength of 210 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	Transverse
-	20 °C	Yield strength of 210 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Yield strength of 220 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	Transverse
-	20 °C	Yield strength of 220 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Yield strength of 240 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	Transverse
-	20 °C	Yield strength of 240 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Yield strength of 260 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	Transverse
-	20 °C	Yield strength of 260 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Yield strength of 270 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	Transverse
-	20 °C	Yield strength of 270 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	20 °C	Yield strength of 275 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	Transverse
-	20 °C	Yield strength of 275 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	-
-	50 °C	Yield strength of 208 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	50 °C	Yield strength of 218 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	50 °C	Yield strength of 238 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	50 °C	Yield strength of 258 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	50 °C	Yield strength of 268 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	50 °C	Yield strength of 273 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	RP02
-	100 °C	Yield strength of 202 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	100 °C	Yield strength of 211 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	100 °C	Yield strength of 230 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	100 °C	Yield strength of 250 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	RP02
-	100 °C	Yield strength of 259 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	100 °C	Yield strength of 264 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	RP02
-	150 °C	Yield strength of 191 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	150 °C	Yield strength of 200 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	150 °C	Yield strength of 218 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	150 °C	Yield strength of 236 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	150 °C	Yield strength of 245 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	150 °C	Yield strength of 250 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	RP02
-	200 °C	Yield strength of 178 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	200 °C	Yield strength of 186 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	200 °C	Yield strength of 203 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	200 °C	Yield strength of 220 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	200 °C	Yield strength of 228 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	200 °C	Yield strength of 233 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	RP02
-	250 °C	Yield strength of 164 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	250 °C	Yield strength of 171 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	250 °C	Yield strength of 186 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	250 °C	Yield strength of 202 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	250 °C	Yield strength of 209 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	250 °C	Yield strength of 213 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	RP02
-	300 °C	Yield strength of 148 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	300 °C	Yield strength of 155 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	300 °C	Yield strength of 169 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	300 °C	Yield strength of 183 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	300 °C	Yield strength of 190 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	300 °C	Yield strength of 194 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	RP02
-	350 °C	Yield strength of 134 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	350 °C	Yield strength of 140 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	350 °C	Yield strength of 153 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	350 °C	Yield strength of 165 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	350 °C	Yield strength of 172 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	350 °C	Yield strength of 175 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	RP02
-	400 °C	Yield strength of 121 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	400 °C	Yield strength of 127 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	400 °C	Yield strength of 139 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	400 °C	Yield strength of 150 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	400 °C	Yield strength of 156 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	400 °C	Yield strength of 159 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	RP02
-	450 °C	Yield strength of 113 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	450 °C	Yield strength of 118 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	450 °C	Yield strength of 129 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	450 °C	Yield strength of 139 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	450 °C	Yield strength of 145 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	450 °C	Yield strength of 147 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat, Sheet	RP02
-	500 °C	Yield strength of 108 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	500 °C	Yield strength of 113 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	500 °C	Yield strength of 123 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	500 °C	Yield strength of 134 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	500 °C	Yield strength of 139 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02
-	500 °C	Yield strength of 141 MPa	normalized or normalized formed (+N)	EN 10028-2	Flat	RP02

We set new standards in steel manufacturing, pushing boundaries to deliver exceptional quality.

-- Our promise

Similar or equivalent steel materials