EN 10216-2 Grade 16Mo3 normalized or normalized formed (+N)
EN 10216-2 Grade 16Mo3 normalized or normalized formed (+N) introduction
Seamless tubes of the high-temperature 16Mo3 are used in steam boiler and pipeline construction, pressure vessel and apparatus engineering, especially in chemical industry and power station construction at temperatures from approx. 200 °C to maximum 400 °C and simultaneously high pressures. The total load and the special scaling circumstances can decrease or increase the temperature limit.
Weldability is available.
Equivalent material: NBN 16Mo3, AFNOR 15D3, BS 243, ISO P26, UNI 16Mo3, ÖNORM 15Mo3KK, PN 16M, SS 2912, UNE F.2601-16Mo3, DIN 15Mo3, GB 15MoG, GB A65158, IS 16Mo30, JIS STPA12, JIS STBA12, KS STHA12, ASTM P1, UNS K11522, DIN 16Mo3, ISO 16Mo3, ASTM A182 Grade F1, ASTM F1, ASTM Grade F1, UNS K12822, DIN 1.5415, AFNOR 16Mo3, BS 16Mo3, JIS STFA12, EN 1.5415, ISO F26, DIN 1.5417, DIN 26Mo2, AFNOR TU 15 03, AFNOR 15 D3, BS 1501-240, UNI 16Mo3KW, UNE 16Mo3, JIS SB480, JIS SB480M, EN 15Mo3, EN 1.5417, ASTM Grade A
EN 10216-2 Grade 16Mo3 normalized or normalized formed (+N) general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.85 - 7.86 g/cm³ |
| - | 50.0 °C | Density of 7.84 g/cm³ |
| - | 100.0 °C | Density of 7.82 g/cm³ |
| - | 150.0 °C | Density of 7.81 g/cm³ |
| - | 200.0 °C | Density of 7.79 g/cm³ |
| - | 250.0 °C | Density of 7.77 g/cm³ |
| - | 300.0 °C | Density of 7.76 g/cm³ |
| - | 350.0 °C | Density of 7.74 g/cm³ |
| - | 400.0 °C | Density of 7.72 g/cm³ |
| - | 450.0 °C | Density of 7.7 g/cm³ |
| - | 500.0 °C | Density of 7.68 g/cm³ |
| - | 550.0 °C | Density of 7.66 g/cm³ |
| - | 600.0 °C | Density of 7.64 g/cm³ |
EN 10216-2 Grade 16Mo3 normalized or normalized formed (+N) thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | -100.0 °C | Coefficient of thermal expansion of 1.05E-5 1/K | - |
| - | 20.0 °C | Coefficient of thermal expansion of 1.15E-5 1/K | - |
| - | 100.0 °C | Coefficient of thermal expansion of 1.21E-5 1/K | - |
| - | 200.0 °C | Coefficient of thermal expansion of 1.27E-5 1/K | - |
| - | 300.0 °C | Coefficient of thermal expansion of 1.32E-5 1/K | - |
| - | 400.0 °C | Coefficient of thermal expansion of 1.36E-5 1/K | - |
| - | 500.0 °C | Coefficient of thermal expansion of 1.4E-5 1/K | - |
| - | 600.0 °C | Coefficient of thermal expansion of 1.44E-5 1/K | - |
| Max service temperature, long | - | Max service temperature, long of 200 - 550 °C | - |
| Melting point | - | Melting point of 1382 - 1529 °C | Typical for Molybdenum Steel |
| Specific heat capacity | -100.0 °C | Specific heat capacity of 423 J/(kg·K) | - |
| - | 20.0 °C | Specific heat capacity of 461 J/(kg·K) | - |
| - | 100.0 °C | Specific heat capacity of 479 J/(kg·K) | - |
| - | 200.0 °C | Specific heat capacity of 499 J/(kg·K) | - |
| - | 300.0 °C | Specific heat capacity of 517 J/(kg·K) | - |
| - | 400.0 °C | Specific heat capacity of 536 J/(kg·K) | - |
| - | 500.0 °C | Specific heat capacity of 558 J/(kg·K) | - |
| - | 600.0 °C | Specific heat capacity of 587 J/(kg·K) | - |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 52.1 W/(m·K) | - |
| - | 100.0 °C | Thermal conductivity of 51.2 W/(m·K) | - |
| - | 200.0 °C | Thermal conductivity of 48.7 W/(m·K) | - |
| - | 300.0 °C | Thermal conductivity of 45.5 W/(m·K) | - |
| - | 400.0 °C | Thermal conductivity of 42.3 W/(m·K) | - |
| - | 500.0 °C | Thermal conductivity of 39.1 W/(m·K) | - |
| - | 600.0 °C | Thermal conductivity of 36 W/(m·K) | - |
| Thermal diffusivity | 20.0 °C | Thermal diffusivity of 14.4 mm²/s | - |
| - | 100.0 °C | Thermal diffusivity of 13.2 mm²/s | - |
| - | 200.0 °C | Thermal diffusivity of 11.7 mm²/s | - |
| - | 300.0 °C | Thermal diffusivity of 10.3 mm²/s | - |
| - | 400.0 °C | Thermal diffusivity of 9 mm²/s | - |
| - | 500.0 °C | Thermal diffusivity of 7.5 mm²/s | - |
| - | 600.0 °C | Thermal diffusivity of 6 mm²/s | - |
EN 10216-2 Grade 16Mo3 normalized or normalized formed (+N) chemical
| Property | Value |
|---|---|
| Aluminium | Aluminium of 0.04 % |
| Carbon | Carbon of 0.12 - 0.2 % |
| Chromium | Chromium of 0.3 % |
| Copper | Copper of 0.3 % |
| Manganese | Manganese of 0.4 - 0.9 % |
| Molybdenum | Molybdenum of 0.25 - 0.35 % |
| Nickel | Nickel of 0.3 % |
| Phosphorus | Phosphorus of 0.03 % |
| Silicon | Silicon of 0.35 % |
| Sulfur | Sulfur of 0.01 - 0.02 % |
EN 10216-2 Grade 16Mo3 normalized or normalized formed (+N) electrical
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 2E-7 - 2.16E-7 Ω·m |
| - | 50.0 °C | Electrical resistivity of 2.37E-7 Ω·m |
| - | 100.0 °C | Electrical resistivity of 2.5E-7 - 2.68E-7 Ω·m |
| - | 150.0 °C | Electrical resistivity of 3.02E-7 Ω·m |
| - | 200.0 °C | Electrical resistivity of 3.24E-7 - 3.39E-7 Ω·m |
| - | 250.0 °C | Electrical resistivity of 3.8E-7 Ω·m |
| - | 300.0 °C | Electrical resistivity of 4.12E-7 - 4.25E-7 Ω·m |
| - | 350.0 °C | Electrical resistivity of 4.74E-7 Ω·m |
| - | 400.0 °C | Electrical resistivity of 5.14E-7 - 5.27E-7 Ω·m |
| - | 450.0 °C | Electrical resistivity of 5.83E-7 Ω·m |
| - | 500.0 °C | Electrical resistivity of 6.33E-7 - 6.42E-7 Ω·m |
| - | 550.0 °C | Electrical resistivity of 7.08E-7 Ω·m |
| - | 600.0 °C | Electrical resistivity of 7.69E-7 - 7.78E-7 Ω·m |
EN 10216-2 Grade 16Mo3 normalized or normalized formed (+N) mechanical
| Property | Temperature | Value |
|---|---|---|
| Elastic modulus | -100.0 °C | Elastic modulus of 217 GPa |
| - | 20.0 °C | Elastic modulus of 212 - 212.48 GPa |
| - | 50.0 °C | Elastic modulus of 211.6 GPa |
| - | 100.0 °C | Elastic modulus of 207 - 209.25 GPa |
| - | 150.0 °C | Elastic modulus of 206.11 GPa |
| - | 200.0 °C | Elastic modulus of 199 - 202.48 GPa |
| - | 250.0 °C | Elastic modulus of 198.36 GPa |
| - | 300.0 °C | Elastic modulus of 192 - 194.14 GPa |
| - | 350.0 °C | Elastic modulus of 189.82 GPa |
| - | 400.0 °C | Elastic modulus of 184 - 185.51 GPa |
| - | 450.0 °C | Elastic modulus of 180.99 GPa |
| - | 500.0 °C | Elastic modulus of 175 - 176.48 GPa |
| - | 550.0 °C | Elastic modulus of 171.97 GPa |
| - | 600.0 °C | Elastic modulus of 164 - 166.97 GPa |
| Elongation | 20.0 °C | Elongation of 22 % |
| Elongation, transverse | 20.0 °C | Elongation, transverse of 20 % |
| Poisson's ratio | 20.0 °C | Poisson's ratio of 0.29 [-] |
| - | 50.0 °C | Poisson's ratio of 0.29 [-] |
| - | 100.0 °C | Poisson's ratio of 0.29 [-] |
| - | 150.0 °C | Poisson's ratio of 0.29 [-] |
| - | 200.0 °C | Poisson's ratio of 0.29 [-] |
| - | 250.0 °C | Poisson's ratio of 0.29 [-] |
| - | 300.0 °C | Poisson's ratio of 0.29 [-] |
| - | 350.0 °C | Poisson's ratio of 0.29 [-] |
| - | 400.0 °C | Poisson's ratio of 0.3 [-] |
| - | 450.0 °C | Poisson's ratio of 0.3 [-] |
| - | 500.0 °C | Poisson's ratio of 0.3 [-] |
| - | 550.0 °C | Poisson's ratio of 0.3 [-] |
| - | 600.0 °C | Poisson's ratio of 0.3 [-] |
| Shear modulus | 20.0 °C | Shear modulus of 82.6 GPa |
| - | 50.0 °C | Shear modulus of 82.21 GPa |
| - | 100.0 °C | Shear modulus of 81.23 GPa |
| - | 150.0 °C | Shear modulus of 79.95 GPa |
| - | 200.0 °C | Shear modulus of 78.48 GPa |
| - | 250.0 °C | Shear modulus of 76.81 GPa |
| - | 300.0 °C | Shear modulus of 75.05 GPa |
| - | 350.0 °C | Shear modulus of 73.38 GPa |
| - | 400.0 °C | Shear modulus of 71.61 GPa |
| - | 450.0 °C | Shear modulus of 69.75 GPa |
| - | 500.0 °C | Shear modulus of 67.98 GPa |
| - | 550.0 °C | Shear modulus of 66.22 GPa |
| - | 600.0 °C | Shear modulus of 64.35 GPa |
| Tensile strength | 20.0 °C | Tensile strength of 450 - 600 MPa |
| Tensile strength, transverse | 20.0 °C | Tensile strength, transverse of 450 - 600 MPa |
| Yield strength | 20.0 °C | Yield strength of 260 - 285 MPa |
| - | 100.0 °C | Yield strength of 243 - 265 MPa |
| - | 150.0 °C | Yield strength of 237 - 252 MPa |
| - | 200.0 °C | Yield strength of 224 - 240 MPa |
| - | 250.0 °C | Yield strength of 205 - 220 MPa |
| - | 300.0 °C | Yield strength of 173 - 195 MPa |
| - | 350.0 °C | Yield strength of 159 - 185 MPa |
| - | 400.0 °C | Yield strength of 156 - 175 MPa |
| - | 450.0 °C | Yield strength of 150 - 170 MPa |
| - | 500.0 °C | Yield strength of 146 - 165 MPa |
| Yield strength Rp0.2 | 20.0 °C | Yield strength Rp0.2 of 260 - 280 MPa |
| - | 100.0 °C | Yield strength Rp0.2 of 243 MPa |
| - | 150.0 °C | Yield strength Rp0.2 of 237 MPa |
| - | 200.0 °C | Yield strength Rp0.2 of 224 MPa |
| - | 250.0 °C | Yield strength Rp0.2 of 205 MPa |
| - | 300.0 °C | Yield strength Rp0.2 of 173 MPa |
| - | 350.0 °C | Yield strength Rp0.2 of 159 MPa |
| - | 400.0 °C | Yield strength Rp0.2 of 156 MPa |
| - | 450.0 °C | Yield strength Rp0.2 of 150 MPa |
| - | 500.0 °C | Yield strength Rp0.2 of 146 MPa |
| Yield strength Rp0.2, transverse | 20.0 °C | Yield strength Rp0.2, transverse of 260 - 280 MPa |
Have confidence in the strength and durability of our steel materials.
-- Our promise
Similar or equivalent steel materials
- EN 10028-2 Grade 16Mo3 normalized or normalized formed (+N)
- EN 10217-2 Grade 16Mo3 normalized or normalized formed (+N)
- EN 10217-5 Grade 16Mo3 normalized or normalized formed (+N)
- DIN 17155 Grade 15Mo3 normalized or normalized formed (+N)
- EN 10222-2 Grade 16Mo3 normalized or normalized formed (+N)
- EN 10222-2 Grade 16Mo3 quenched and tempered (+QT)
- EN 10273 Grade 16Mo3 normalized or normalized formed (+N)
- JIS G3444 Grade STK490
- JIS G3444 Grade STK500
- JIS G3454 Grade STPG370