JIS G3455 Grade STS370
Equivalent material: DIN 1.0255, DIN St 37-4, DIN St 37.4, AFNOR TU E 220, BS P235T2, JIS STPY400, EN P235T2, EN P235TR2, EN 1.0255, ASTM Grade A, AFNOR TS 37 CP, ASTM Grade Y 35
JIS G3455 Grade STS370 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
JIS G3455 Grade STS370 thermal
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 16 - 30 % |
- |
| Elongation A5, transverse |
23.0 °C |
Elongation A5, transverse of 23 - 25 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 370 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 215 MPa |
- |
JIS G3455 Grade STS370 chemical
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
JIS G3455 Grade STS370 magnetic
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
JIS G3455 Grade STS370 electrical
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
JIS G3455 Grade STS370 mechanical
| Property |
Value |
| Wall thickness |
Wall thickness of 1 - 8 mm |