ASTM A182 Grade F1 Annealed or Normalized and Tempered
Equivalent material: ASTM Grade F1, UNS K12520
ASTM A182 Grade F1 Annealed or Normalized and Tempered general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Molybdenum Steel |
ASTM A182 Grade F1 Annealed or Normalized and Tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.29E-5 1/K |
Typical for Molybdenum Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Molybdenum Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 456 J/(kg·K) |
Typical for Molybdenum Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 37 - 48 W/(m·K) |
Typical for Molybdenum Steel |
ASTM A182 Grade F1 Annealed or Normalized and Tempered chemical
| Property |
Value |
| Carbon |
Carbon of 0.28 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Molybdenum |
Molybdenum of 0.44 - 0.65 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 0.15 - 0.35 % |
| Sulfur |
Sulfur of 0.045 % |
ASTM A182 Grade F1 Annealed or Normalized and Tempered mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Molybdenum Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 20 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 143 - 192 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Molybdenum Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 30 % |
- |
| Tensile strength |
23.0 °C |
Tensile strength of 485 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 275 MPa |
- |