ASTM A1011 Grade CS Type B
Equivalent material: DIN 1.0241, DIN FeE220G, DIN S220GD, AFNOR S220GD, BS S220GD, EN S220GD, EN 1.0241, ISO 220, GOST 220, GB/T S220GD, DIN 1.0332, DIN StW 22, DIN DC11, AFNOR DC11, AFNOR 1C, BS DC11, BS 4CS, BS 4HS, BS 4CR, AISI 1008, SAE 1008, JIS SPHC, JIS SPHD, JIS SEHD, EN DD11, EN 1.0332, ISO HR2, GOST 15kp
ASTM A1011 Grade CS Type B general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ASTM A1011 Grade CS Type B thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
ASTM A1011 Grade CS Type B chemical
| Property |
Value |
| Carbon |
Carbon of 0.02 - 0.15 % |
| Chromium |
Chromium of 0.15 % |
| Copper |
Copper of 0.2 % |
| Manganese |
Manganese of 0.6 % |
| Molybdenum |
Molybdenum of 0.06 % |
| Nickel |
Nickel of 0.2 % |
| Niobium |
Niobium of 8E-3 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Sulfur |
Sulfur of 0.035 % |
| Titanium |
Titanium of 0.03 % |
| Vanadium |
Vanadium of 8E-3 % |
ASTM A1011 Grade CS Type B magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ASTM A1011 Grade CS Type B electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A1011 Grade CS Type B mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 25 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 75 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Yield strength |
23.0 °C |
Yield strength of 205 - 340 MPa |
- |