EN 10111 Grade DD11 hot rolled
EN 10111 Grade DD11 hot rolled introduction
Deoxidation method at manufacturer`s option.
The material meets deep drawing quality requirements.
Suitability for welding according to common methods.
The steel is suitable for application of surface coatings.
Equivalent material: AFNOR 1C, BS HR3, BS HR4, BS HS4, UNI FeP11, UNE AP11, ASTM CSTypeB, DIN StW22, AS HA1, IS HR2, IS SPHC, IS SPHD, GOST 15kp, GOST 15кп, ASTM A1011CSTypeB, DIN 1.0332, EN DC11, EN FeP11, EN 1.0332, DIN StW 22, DIN DD11, DIN DC11, AFNOR DC11, AISI 1008, BS DC11, BS 4CS, BS 4HS, BS 4CR, SAE 1008, JIS SPHC, JIS SPHD, JIS SEHD, ISO HR2, ASTM CS Type B, ASTM 1008
EN 10111 Grade DD11 hot rolled general
| Property |
Value |
Comment |
| Density |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10111 Grade DD11 hot rolled thermal
| Property |
Value |
Comment |
| Coefficient of thermal expansion |
Coefficient of thermal expansion of 1.32e-05 - 1.38e-05 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
Max service temperature of 314.3 °C |
Predicted Value, Long |
| - |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
EN 10111 Grade DD11 hot rolled chemical
| Property |
Value |
Condition |
Related Standards |
Shape |
| Carbon |
Carbon of 0.12 % |
hot rolled |
EN 10111 |
Flat |
| Manganese |
Manganese of 0.6 % |
hot rolled |
EN 10111 |
Flat |
| Phosphorus |
Phosphorus of 0.045 % |
hot rolled |
EN 10111 |
Flat |
| Sulfur |
Sulfur of 0.045 % |
hot rolled |
EN 10111 |
Flat |
EN 10111 Grade DD11 hot rolled magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10111 Grade DD11 hot rolled electrical
| Property |
Value |
Comment |
| Electrical conductivity |
Electrical conductivity of 8 S/m |
Predicted Value |
| Electrical resistivity |
Electrical resistivity of 1.43e-07 - 1.74e-07 Ω·m |
Typical for Carbon Steel |
EN 10111 Grade DD11 hot rolled mechanical
| Property |
Value |
Comment |
| Elastic modulus |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Hardness, Brinell |
Hardness, Brinell of 267 [-] |
Predicted Value, Transverse |
| Poisson's ratio |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Reduction of area |
Reduction of area of 41.2 % |
Predicted Value |
| - |
Reduction of area of 44.1 % |
Predicted Value, Transverse |
| Shear modulus |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Shear strength |
Shear strength of 527.3 MPa |
Predicted Value |
From concept to completion, we deliver excellence in every aspect of the steel supply chain.
-- Our promise