AISI 301 1/8-Hard
Equivalent material: SAE 301, JIS SUS301, ASTM MT301, ASTM 301, UNS S30100, DIN 1.4310, DIN X12CrNi-17-7, DIN O, DIN 14, DIN X10CrNi18-8, DIN X12CrNi17-7, DIN X 12 CrNi 17 7, AFNOR X10CrNi18-8, AFNOR Z12CN17-07, BS 301S21, BS X10CrNi18-8, UNI X2CrNi1807, SS 2331, UNE F.3517, AISI S30100, AISI 30301, SAE S30100, SAE 30301, JIS SUS302, EN X10CrNi18-8, EN 1.4310, ISO X10CrNi18-8, GOST 12Ch18N9, GB 1Cr17Ni7, ASTM S30151, ASTM 30302, UNS S30200, UNS S30151, IS X07Cr18Ni9, DIN 1.4324, AISI 302, SAE 302, JIS SUS301J1, EN FE-PA 18, EN 1.4324, 302, ASTM MT302
AISI 301 1/8-Hard general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
AISI 301 1/8-Hard thermal
| Property |
Temperature |
Value |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 1/K |
| Melting point |
- |
Melting point of 1400 °C |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 500 J/(kg·K) |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 15 W/(m·K) |
AISI 301 1/8-Hard chemical
| Property |
Value |
| Carbon |
Carbon of 0 - 0.15 % |
| Chromium |
Chromium of 16 - 19 % |
| Iron |
Iron of 66.4 - 78 % |
| Manganese |
Manganese of 0 - 2 % |
| Molybdenum |
Molybdenum of 0 - 0.8 % |
| Nickel |
Nickel of 6 - 9.5 % |
| Nitrogen |
Nitrogen of 0 - 0.1 % |
| Phosphorus |
Phosphorus of 0 - 0.05 % |
| Silicon |
Silicon of 0 - 2 % |
| Sulfur |
Sulfur of 0 - 0.03 % |
AISI 301 1/8-Hard electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
AISI 301 1/8-Hard mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 46 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 790 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 440 MPa |
- |