JIS G4303 Grade SUS301 solution treated
Equivalent material: GB/T 1Cr17Ni7, GB/T 1Cr17Ni7, GB 1Cr17Ni7, GB 1Cr17Ni8, AS 301, DIN X12CrNi177, NF Z12CN17-07, NF Z12CN18-07, NF Z11CN17-08, NF Z1118-08, NF Z12CN18-09, BS 801A, BS 801AM, BS 301S21, IS 10Cr17Ni7, UNI X12CrNi1707, EN X10CrNi18-8, UNE X12CrNi177, SIS 2331-02, SIS 2331-06, SIS 2331-16, SIS 2331-11, SIS 2331-12, SIS 2331-14, SIS 2331-17, SIS 2331-18, SIS 2331-19, SIS 2331, AMS 5517, AMS 5518, AMS 5519, ASTM 301, ASTM MT301, MIL 301, AISI 301, SAE 301, UNS S30100, DIN 1.4310, DIN X12CrNi-17-7, DIN O, DIN 14, DIN X10CrNi18-8, DIN X12CrNi17-7, DIN X 12 CrNi 17 7, AFNOR X10CrNi18-8, AFNOR Z12CN17-07, BS X10CrNi18-8, UNI X2CrNi1807, SS 2331, UNE F.3517, AISI S30100, AISI 30301, SAE S30100, SAE 30301, JIS SUS302, EN 1.4310, ISO X10CrNi18-8, GOST 12Ch18N9, ASTM S30151, ASTM 30302, UNS S30200, UNS S30151, IS X07Cr18Ni9
JIS G4303 Grade SUS301 solution treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4303 Grade SUS301 solution treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4303 Grade SUS301 solution treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4303 Grade SUS301 solution treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 40 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 207 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 95 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 218 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 60 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 520 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |