JIS G4305 Grade SUS301J1 solution treated

Equivalent material: DIN 1.4324, AISI 301, AISI 302, SAE 301, SAE 302, EN FE-PA 18, EN 1.4324, ASTM 301, 302, ASTM MT302, ASTM MT301, UNS S30200

JIS G4305 Grade SUS301J1 solution treated general

Property	Temperature	Value	Comment
Density	23.0 °C	Density of 7.9 - 8.2 g/cm³	Typical for Austenitic Stainless Steel

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K	Typical for Austenitic Stainless Steel
Melting point	-	Melting point of 1230 - 1480 °C	Typical for Austenitic Stainless Steel
Specific heat capacity	23.0 °C	Specific heat capacity of 440 J/(kg·K)	Typical for Austenitic Stainless Steel
Thermal conductivity	23.0 °C	Thermal conductivity of 11 - 21 W/(m·K)	Typical for Austenitic Stainless Steel

Property	Temperature	Value	Comment
Electrical resistivity	23.0 °C	Electrical resistivity of 8.5E-7 Ω·m	Typical for Austenitic Stainless Steel

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	Elastic modulus of 195 GPa	Typical for Austenitic Stainless Steel
Elongation A5	23.0 °C	Elongation A5 of 45 %	-
Hardness, Brinell	23.0 °C	Hardness, Brinell of 187 [-]	-
Hardness, Rockwell B	23.0 °C	Hardness, Rockwell B of 90 [-]	-
Hardness, Vickers	23.0 °C	Hardness, Vickers of 200 [-]	-
Poisson's ratio	23.0 °C	Poisson's ratio of 0.3 [-]	Typical for Austenitic Stainless Steel
Shear modulus	23.0 °C	Shear modulus of 77 GPa	Typical for Austenitic Stainless Steel
Tensile strength	23.0 °C	Tensile strength of 570 MPa	-
Yield strength Rp0.2	23.0 °C	Yield strength Rp0.2 of 205 MPa	-