JIS G4306 Grade SUS301 cold-rolled, solution annealed
Equivalent material: GB/T 1Cr17Ni7, GB/T 1Cr17Ni7, GB 1Cr17Ni7, GB 1Cr17Ni8, AS 301, DIN X12CrNi177, NF Z12CN17-07, NF Z12CN18-07, NF Z11CN17-08, NF Z1118-08, NF Z12CN18-09, BS 801A, BS 801AM, BS 301S21, IS 10Cr17Ni7, UNI X12CrNi1707, EN X10CrNi18-8, UNE X12CrNi177, SIS 2331-02, SIS 2331-06, SIS 2331-16, SIS 2331-11, SIS 2331-12, SIS 2331-14, SIS 2331-17, SIS 2331-18, SIS 2331-19, SIS 2331, AMS 5517, AMS 5518, AMS 5519, ASTM 301, ASTM MT301, MIL 301, AISI 301, SAE 301, JIS SUS301, UNS S30100, DIN 1.4310, DIN X12CrNi-17-7, DIN O, DIN 14, DIN X10CrNi18-8, AFNOR X10CrNi18-8, BS X10CrNi18-8, UNI X2CrNi1807, SS 2331, UNE F.3517, AISI S30100, AISI 30301, SAE S30100, SAE 30301, JIS SUS302, EN 1.4310, ISO X10CrNi18-8, GOST 12Ch18N9, ASTM S30151, ASTM 30302, UNS S30200, UNS S30151, IS X07Cr18Ni9
JIS G4306 Grade SUS301 cold-rolled, solution annealed general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4306 Grade SUS301 cold-rolled, solution annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1375 - 1450 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4306 Grade SUS301 cold-rolled, solution annealed chemical
| Property |
Value |
| Carbon |
Carbon of 0.15 % |
| Chromium |
Chromium of 16 - 18 % |
| Iron |
Iron of 70.78 - 78 % |
| Manganese |
Manganese of 2 % |
| Nickel |
Nickel of 6 - 8 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
JIS G4306 Grade SUS301 cold-rolled, solution annealed electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4306 Grade SUS301 cold-rolled, solution annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation |
20.0 °C |
Elongation of 40 % |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 520 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 206 MPa |
- |