UGIMA®-X 4305 Cold Drawn
UGIMA®-X 4305 Cold Drawn introduction
UGIMA®-X 4305 is a stainless steel of highly improved machinability manufactured only by Ugitech.
Its properties are identical to those of other 1.4305s except for its machinability, which is even better than that of UGIMA® 4305, the 1.4305 grade from Ugitech with already improved machinability.
UGIMA®-X 4305 is a stainless steel resulting from an improved production and control process in the UGIMA® population developed by Ugitech.
UGIMA®-X 4305 represents a technological advance which has advantages whatever the machining conditions, machinery or tools used, its machinability is optimal at high cutting conditions.
Compared to UGIMA® 4305, increases of 15% have been achieved in turning. This ranks it slightly ahead of UGIMA® 4305 HM, with fewer detrimental effects such as the cold cracking phenomenon thanks to its lower sulfur content.
Equivalent material: EN 1.4305, EN X8CrNiS18-9, UNS S30300, JIS SUS303, ISO 4305-303-00-I, ISO X10CrNiS18-9, AISI 303, AFNOR Z8CNF18-09, DIN 1.4305, DIN X8CrNiS18-9, BS 303S31, SS 2346
UGIMA®-X 4305 Cold Drawn general
| Property |
Value |
| Density |
Density of 7.9 g/cm³ |
UGIMA®-X 4305 Cold Drawn thermal
| Property |
Value |
Comment |
| Coefficient of thermal expansion |
Coefficient of thermal expansion of 0.0000168 1/K |
20 to 200°C |
| Specific heat capacity |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
Thermal conductivity of 15.3 W/(m·K) |
- |
UGIMA®-X 4305 Cold Drawn chemical
| Property |
Value |
Comment |
| Carbon |
Carbon of 0.07 |
max. |
| Chromium |
Chromium of 17.0 - 18.0 % |
- |
| Copper |
Copper of 0.75 |
max. |
| Manganese |
Manganese of 2.0 |
max. |
| Molybdenum |
Molybdenum of 0.5 |
max. |
| Nickel |
Nickel of 8.0 - 10.0 % |
- |
| Phosphorus |
Phosphorus of 0.04 |
max. |
| Silicon |
Silicon of 0.75 |
max. |
| Sulfur |
Sulfur of 0.25 - 0.35000000000000003 % |
- |
UGIMA®-X 4305 Cold Drawn electrical
| Property |
Value |
| Electrical resistivity |
Electrical resistivity of 7.3e-07 Ω·m |
UGIMA®-X 4305 Cold Drawn mechanical
| Property |
Value |
| Elastic modulus |
Elastic modulus of 196 GPa |
| Elongation |
Elongation of 26.0 - 47.0 % |
| Reduction of area |
Reduction of area of 37.0 - 56.0 % |
| Tensile strength |
Tensile strength of 685.0 - 850.0 MPa |
UGIMA®-X 4305 Cold Drawn application
| Property |
- |
- |
| Application areas |
| Corrosion properties |
Environment |
Behavior |
| Nitric acid |
Good |
| Phosphoric acid |
Average |
| Sulfuric acid |
Average |
| Acetic acid |
Average |
| Sodium carbonate |
Average |
| NaCl (Saline mist) |
Average |
| Humidity |
Good |
| Sea water |
Restricted use |