UGICHROM® 4305
UGICHROM® 4305 introduction
UGICHROM® is the result of combining the high efficiency of micro-fissuring chromium plating with the technology of the most advanced stainless steel bars. The UGICHROM® product range is recommended for hydraulic and pneumatic mechanisms.
General properties - choice for performance:
Low friction coefficient.
High resistance to wear.
Increased corrosion resistance.
Micro-fissuring chromium plating guarantees excellent performance under extreme conditions of service.
Improved machinability (up to +20% of productivity).
High mechanical properties.
Accurate geometrical and dimensional properties..
Equivalent material: EN 1.4305, EN X8CrNis18-9, DIN 1.4305, DIN X8CrNis18-9, AISI 303
UGICHROM® 4305 general
| Property |
Value |
| Density |
Density of 7.9 g/cm³ |
UGICHROM® 4305 thermal
| Property |
Value |
Comment |
| Coefficient of thermal expansion |
Coefficient of thermal expansion of 0.0000168 1/K |
20 to 200°C |
| Specific heat capacity |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
Thermal conductivity of 15.3 W/(m·K) |
- |
UGICHROM® 4305 chemical
| Property |
Value |
Comment |
| Carbon |
Carbon of 0.07 |
max. |
| Chromium |
Chromium of 17.0 - 18.0 % |
- |
| Manganese |
Manganese of 1.5 - 2.0 % |
- |
| Molybdenum |
Molybdenum of 0.5 |
max. |
| Nickel |
Nickel of 8.2 - 9.5 % |
- |
| Niobium |
Niobium of 0.45 |
max., min: 5xC |
| Phosphorus |
Phosphorus of 0.04 |
max. |
| Silicon |
Silicon of 0.75 |
max. |
| Sulfur |
Sulfur of 0.25 - 0.35000000000000003 % |
- |
UGICHROM® 4305 electrical
| Property |
Value |
| Electrical resistivity |
Electrical resistivity of 7.3e-07 Ω·m |
UGICHROM® 4305 mechanical
| Property |
Value |
Comment |
| Elastic modulus |
Elastic modulus of 196 GPa |
- |
| Tensile strength |
Tensile strength of 500 MPa |
min. |
UGICHROM® 4305 application
| Property |
- |
- |
| Application areas |
| Corrosion properties |
| Other |
CHARACTERISTICS |
Standard product |
Special product |
| Diameter tolerance |
ISO f7 |
On request |
| Bar length dia. 12 to 19 mm |
2900 mm +200/-0 |
On request |
| Bar length dia. 20 to 125 mm |
6000 mm +/- 500 mm |
On request |
| Roundness |
<1/2 f7 ISO |
- |
| Straightness (to EN 10278) |
<0.5 mm/ml |
Up to 0.2 mm for dia. >30 mm |
| Roughness |
Ra < 0.2 µm |
Up to Ra <0.08 µm |
| Chromium structure |
Microcracked |
- |
| Sizes |
Dia. 12 to 125 mm |
On request |
| Thickness of the chromium dia. 12 to 19.5 mm |
18 µm +/-3 |
Max. 50 µm |
| Thickness of the chromium dia. 20 to 115 mm |
25 µm +/-5 |
Max. 100 µm |