JIS G4303 Grade SUS303 solution treated
Equivalent material: GB/T Y1Cr18Ni9, GB/T Y1Cr18Ni9-Q, GB/T Y1Cr18Ni9-R, GB Y1Cr18Ni9, AS 303, DIN X10CrNiS189, NF Z8CNF18-09, BS 303S21, BS 303S31, BS 303S22, UNI X10CrNiS1809, EN X8CrNiS18-9, UNE X10CrNiS189, UNE F.310.C, SIS 2346-02, SIS 2346, AMS 5640, ASME 303, ASTM B8F, ASTM 303, ASTM 8F with S, ASTM 8FA with S, MIL 303, AISI 303, DIN 1.4305, DIN X 10 CrNiS 18 9, DIN X8CrNiS18-9, DIN X10CrNiS18-9, AFNOR Z8CNF18-09, BS EN58M, SS 2346, UNE F.3508, SAE 303, EN 1.4305, ISO A1, GOST 12X18H10E, ASTM Type 303, UNS S30300
JIS G4303 Grade SUS303 solution treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4303 Grade SUS303 solution treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4303 Grade SUS303 solution treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4303 Grade SUS303 solution treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 40 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 187 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 90 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 200 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 50 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 520 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |