UGIMA® 4567 Annealed
UGIMA® 4567 Annealed introduction
Excellent resistance to cold forming due to the contribution of copper: very good behaviour for thread forming and tapping by rolling. Ideal grade for deep drilling. Slightly better corrosion resistance than UGIMA® 4307 due to its copper content.
Equivalent material: EN 1.4567, EN X3CrNiCu18-9-4, DIN 1.4567, DIN X3CrNiCu18-9-4, AISI 304Cu
UGIMA® 4567 Annealed general
| Property |
Value |
Comment |
| Elongation |
Elongation of 25.0 - 40.0 % |
min., depending on the size |
| Tensile strength |
Tensile strength of 430.0 - 850.0 MPa |
depending on the size |
UGIMA® 4567 Annealed thermal
| Property |
- |
- |
| Application areas |
| Corrosion properties |
| Other |
Product |
Shape |
Surface finish |
Tolerance |
Dimension |
| Round |
Rolled and descaled |
12 to 13 |
22 to 130 mm |
| Round |
Turned and polished |
9 to 11 |
22 to 130 mm |
| Round |
Drawn |
8 to 9 |
1.8 to 55 mm |
| Round |
Ground |
7 to 9 |
1.8 to 80 mm |
| Hexagonal |
Drawn |
11 |
3 to 55 mm |
| Drawn wire |
Round |
Mat |
- |
1 to 14 mm |
UGIMA® 4567 Annealed chemical
| Property |
Value |
Comment |
| Carbon |
Carbon of 0.04 |
max. |
| Chromium |
Chromium of 18.0 % |
- |
| Molybdenum |
Molybdenum of 0.4 % |
- |
| Nickel |
Nickel of 9.5 % |
- |
| Sulfur |
Sulfur of 3.5 % |
- |
Let our steel inspire you to innovate, create, and excel in your industry.