EN 10269 Grade X3CrNiCu18-9-4 solution annealed (+AT)
EN 10269 Grade X3CrNiCu18-9-4 solution annealed (+AT) introduction
Trademark X3CrNiCu18-9-4 is comparable to X 3 CrNiCu 18 9 acc. to DIN 1654-5 : 1989-10. The austenitic stainless steel with a low C-content is used for special applications, such as wire for cold heading also at low temperatures. The steel is resistant to intercrystalline corrosion also in sensitized condition.
Application for mounting elements at increased temperatures.
Equivalent material: GB 0Cr18Ni9Cu3, AFNOR Z2CNU18-10, BS 394S17, ISO D32, JIS SUSXM7, DIN X3CrNiCu18-9, UNS S30430, GB 06Cr18Ni9Cu3, GB S30488, DIN 1.4567, DIN X3CrNiCu18-9-4, AFNOR Z3CNU18-10, AFNOR X3CrNiCu18-9-4, BS X3CrNiCu18-9-4, AISI 304Cu, AISI EV-17, SAE 304Cu, SAE EV-17, JIS SUS304J3, JIS SUS304J1, EN 1.4567, ISO X3CrNiCu18-9-4, GB/T 06Cr18Ni9Cu3, GB/T S30488, ASTM S30430
EN 10269 Grade X3CrNiCu18-9-4 solution annealed (+AT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.9 - 7.92 g/cm³ |
EN 10269 Grade X3CrNiCu18-9-4 solution annealed (+AT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.61E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.67E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.72E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.77E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.81E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.84E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.88E-5 1/K |
- |
| - |
700.0 °C |
Coefficient of thermal expansion of 1.91E-5 1/K |
- |
| - |
800.0 °C |
Coefficient of thermal expansion of 1.94E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 440 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 472 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 487 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 503 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 512 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 520 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 530 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 541 J/(kg·K) |
- |
| - |
700.0 °C |
Specific heat capacity of 551 J/(kg·K) |
- |
| - |
800.0 °C |
Specific heat capacity of 559 J/(kg·K) |
- |
| Thermal conductivity |
-100.0 °C |
Thermal conductivity of 11.7 W/(m·K) |
- |
| - |
20.0 °C |
Thermal conductivity of 14.5 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 16 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 17.6 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 19.1 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 20.4 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 21.9 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 23.3 W/(m·K) |
- |
| - |
700.0 °C |
Thermal conductivity of 24.7 W/(m·K) |
- |
| - |
800.0 °C |
Thermal conductivity of 26.1 W/(m·K) |
- |
| Thermal diffusivity |
-100.0 °C |
Thermal diffusivity of 3.7 mm²/s |
- |
| - |
20.0 °C |
Thermal diffusivity of 3.9 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 4.3 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 4.3 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 4.6 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 4.7 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 4.9 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 5 mm²/s |
- |
| - |
700.0 °C |
Thermal diffusivity of 5.3 mm²/s |
- |
| - |
800.0 °C |
Thermal diffusivity of 5.7 mm²/s |
- |
EN 10269 Grade X3CrNiCu18-9-4 solution annealed (+AT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.04 % |
| Chromium |
Chromium of 17 - 19 % |
| Copper |
Copper of 3 - 4 % |
| Manganese |
Manganese of 2 % |
| Nickel |
Nickel of 8.5 - 10.5 % |
| Nitrogen |
Nitrogen of 0.1 - 0.11 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 - 0.03 % |
EN 10269 Grade X3CrNiCu18-9-4 solution annealed (+AT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
-100.0 °C |
Electrical resistivity of 5.86E-7 Ω·m |
| - |
20.0 °C |
Electrical resistivity of 6.92E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 7.58E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 8.36E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 9.07E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 9.73E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 1.02E-6 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 1.06E-6 Ω·m |
| - |
700.0 °C |
Electrical resistivity of 1.1E-6 Ω·m |
| - |
800.0 °C |
Electrical resistivity of 1.13E-6 Ω·m |
EN 10269 Grade X3CrNiCu18-9-4 solution annealed (+AT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 206 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 196 - 200 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 190 - 194 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 182 - 186 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 174 - 179 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 166 - 172 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 158 - 165 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 150 GPa |
- |
| - |
700.0 °C |
Elastic modulus of 142 GPa |
- |
| - |
800.0 °C |
Elastic modulus of 134 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 45 % |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.28 [-] |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 450 - 650 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 175 MPa |
- |