SAE J775 Grade EV-17 For Mechanical Tests: ST+CW
Equivalent material: DIN 1.4567, DIN X3CrNiCu18-9, DIN X3CrNiCu18-9-4, AFNOR Z3CNU18-10, AFNOR X3CrNiCu18-9-4, BS 394S17, BS X3CrNiCu18-9-4, AISI 304Cu, AISI EV-17, SAE 304Cu, JIS SUSXM7, JIS SUS304J3, JIS SUS304J1, EN X3CrNiCu18-9-4, EN 1.4567, ISO X3CrNiCu18-9-4, GB/T 06Cr18Ni9Cu3, GB/T S30488, ASTM S30430, UNS S30430
SAE J775 Grade EV-17 For Mechanical Tests: ST+CW general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.9 g/cm³ |
SAE J775 Grade EV-17 For Mechanical Tests: ST+CW thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
200.0 °C |
Coefficient of thermal expansion of 1.73E-5 1/K |
The mentioned values are between 20°C and the mentioned temperature |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.78E-5 1/K |
The mentioned values are between 20°C and the mentioned temperature |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 16.3 W/(m·K) |
- |
SAE J775 Grade EV-17 For Mechanical Tests: ST+CW chemical
| Property |
Value |
Comment |
| Carbon |
Carbon of 0.1 % |
- |
| Chromium |
Chromium of 17 - 19 % |
- |
| Copper |
Copper of 3 - 4 % |
- |
| Iron |
Iron of 63.9 - 72 % |
Balance |
| Manganese |
Manganese of 2 % |
- |
| Nickel |
Nickel of 8 - 10 % |
- |
| Phosphorus |
Phosphorus of 0.05 % |
- |
| Silicon |
Silicon of 1 % |
- |
| Sulfur |
Sulfur of 0.03 % |
- |
SAE J775 Grade EV-17 For Mechanical Tests: ST+CW electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
SAE J775 Grade EV-17 For Mechanical Tests: ST+CW mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 194 GPa |
- |
| Elongation A5 |
23.0 °C |
Elongation A5 of 17 % |
- |
| Hardness, Rockwell C |
23.0 °C |
Hardness, Rockwell C of 24 - 30 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 1000 - 1150 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 900 - 1000 MPa |
- |