JIS G5102 Grade SCW480

Equivalent material: AS C3, BS 161-430, BS AM1, BS AM2, UNI FeGS52, ASTM WCA, DIN 1.1120, DIN G19Mn5, DIN GS-20Mn5, DIN G20Mn5, EN 1.1120

JIS G5102 Grade SCW480 general

Property	Temperature	Value	Comment
Density	23.0 °C	Density of 7.8 - 7.9 g/cm³	Typical for Low Carbon Steel

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K	Typical for Low Carbon Steel
Max service temperature	-	Max service temperature of 500 °C	Typical for Carbon Steel
Melting point	-	Melting point of 1480 - 1526 °C	Typical for Low Carbon Steel
Specific heat capacity	23.0 °C	Specific heat capacity of 465 J/(kg·K)	Typical for Low Carbon Steel
Thermal conductivity	23.0 °C	Thermal conductivity of 25 - 93 W/(m·K)	Typical for Low Carbon Steel

Property	Value	Comment
Curie temperature	Curie temperature of 770 °C	Typical for Low Carbon Steel

Property	Temperature	Value	Comment
Electrical resistivity	23.0 °C	Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m	Typical for Carbon Steel

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	Elastic modulus of 200 - 215 GPa	Typical for Low Carbon Steel
Elongation A5	23.0 °C	Elongation A5 of 20 %	-
Impact strength, Charpy notched	0.0 °C	Impact strength, Charpy notched of 27 kJ/m²	-
Poisson's ratio	23.0 °C	Poisson's ratio of 0.29 [-]	Typical for Low Carbon Steel
Shear modulus	23.0 °C	Shear modulus of 82 GPa	Typical for Low Carbon Steel
Tensile strength	23.0 °C	Tensile strength of 480 MPa	-
Yield strength Rp0.2	23.0 °C	Yield strength Rp0.2 of 275 MPa	-